研究了A3钢以及16Mn钢经预腐蚀处理,置于北京大气腐蚀曝晒站长期曝晒1 a、2 a后的腐蚀产物的组成.结果表明:尽管预污染气氛不同,曝晒时间不同,但腐蚀产物具有相似的组成,而且主要都由α型羟基氧化铁、γ型羟基氧化铁和δ型羟基氧化铁组成.相同条件下,曝晒1 a与2 a的腐蚀产物组成基本相同;两种碳钢曝晒后内层腐蚀产物的组成基本相同,但外层有所不同.
参考文献
| [1] | Zhang J Y, Yu D S, Zhang Y. Introduction to Corrosionand Protection of Metals, Singapore: International Trans lation Press, 1992:226(张九源,俞东升,张殷.金属腐蚀学导论,新加坡:国际翻译出版社,1992:226) |
| [2] | Ailor W. H. Atmospheric Corrosion. New York, John Wiley and Sons, 1982:8 |
| [3] | Balbaud F, Sanchez G, Fauvet P, Santarini G, Picard G. Corros Sci, 2000; 42:1685 |
| [4] | Shastry C R, Friel J J, Townsnd H E. ASTM STP965, 1988:5 |
| [5] | Wan Y, Shi Z M, Yah C W, Cao C N. Chin J Mater Res, 2002; 16(1: 27(万晔,史志明,严川伟,曹楚南.材料研究学报,2002;16(1:27) |
| [6] | Misawa T, Asami K, Hshimoto K, Shimodaira S. Corros Sci, 1974; 14:279 |
| [7] | Marco J F, Gracia M, Gancedo J R, Martinluengo M A, Joseph G. Corros Sci, 2000; 42:753 |
| [8] | Suzuki I, Hisamatsu Y, Masuko N. J Electrochem Soc, 1980; 127:2210 |
| [9] | Yamashita M, Miyuki H, Matsuda Y, Nagano H, Misawa T. Corros Sci, 1994; 36(2: 291 |
| [10] | Raman A, Kuban B, Razvan A. Corros Sci, 1991; 32(12: 1295 |
| [11] | Wu J G. Techniques and Applications of Infrared FourierTransform Spectroscopy. Beijing: Science and Technology Information Press, Vol.2, 1994:271(吴瑾光.近代傅立叶变换红外光谱技术及应用,北京:科学技术文献出版社,下卷,1994:271 |
| [12] | Nyquist R A, Kagel R O. Infrared Spectra of InorganicCompounds. New York and London: Academic Press, 1971:219 |
| [13] | Nishimura T. Katayama H. Noda K, Kodama T. Corros,2000; 56(9): 936 |
| [14] | Marco J F, Gracia M, Gancedo J R, Martinluengo M A,Joseph G. Corros Sci, 2000; 42:762 |
| [15] | Oh S J, Cook D C, Townsend H E. Corros Sci, 1999; 41:1690 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%