Cu3Au在腐蚀或应力腐蚀时表层Cu原子择优溶解形成脱合金疏松层.对具有疏松层的三维晶体(约148000个原子),用镶嵌原子方法(EAM)势进行了分子动力学模拟.结果表明,一旦出现疏松层就会产生一个拉应力,它使单端固定、单边存在疏松层的晶体发生弯曲,其挠度(或拉应力)随疏松层增厚以及空位浓度升高而升高.
参考文献
[1] | Chu W Y, Qiao L J, Chen Q Z, Gao K W. Fracture and Environment Fracture. Beijing: Science Press, 2000:156(褚武扬,乔利杰,陈奇志,高克玮.断裂和环境断裂.北京:科学出版社,2000:156) |
[2] | Jones D A. Corrosion, 1996; 52:356 |
[3] | Maguin T, Chieragatti R, Bayle B. Acta Mater, 1996; 44:1457 |
[4] | Kanfman M J, Fink T L. Acta Metall, 1988; 36:2213 |
[5] | Gu B, Zhang J W, Wan F Y, Chu W Y. Scr Metall Mater,1995; 32:637 |
[6] | Gao K W, Chu W Y, Gu B, Qiao L J. Corrosion, 2000;56:515 |
[7] | Lu H, Gao K W, Chu W Y. Corros Sci, 1998; 40:1663 |
[8] | Lu H, Gao K W, Wang Y B, Chu W Y. Corrosion, 2000;56:1112 |
[9] | Guo X Z, Gao K W, Qiao L J, Chu W Y. Metall Mater Trans A, 2001; 32:1309 |
[10] | Kevin M, Ferrari M. Mater Sci Eng A, 1997; A232:88 |
[11] | Zhou G H, Lu H, Wan F R, Chu W Y. Acta Mech Sin,1997; 14(4): 377 |
[12] | Ackland G J, Vitek V. Phy Rev B, 1990-Ⅱ; 41:10324 |
[13] | Cassagne T B, Flanagan W F, Lichter B D. Metall Trans A, 1988; 19A: 281 |
[14] | Chen T S, Salmeron M, Devine T M. Corros Sci, 1993;34:2071 |
[15] | Finnis M W, Sinclair J E. Philos Mag A, 1984; 50(1): 45 |
[16] | Toxvaerd Soren. J Comput Phys, 1982; 47:444 |
[17] | Vol A E, Kagan I K. Handbook of binary metallic system structure and properties, Vol. 3, New Delhi: Oxonian Press PVT. Ltd., 1986:117 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%