采用着色腐蚀技术显示出过共晶球铁中的高温凝固组织,观察分析过共晶球铁凝固过程中奥氏体的生长方式与形貌特征.结果表明:在非平衡凝固条件下,过共晶球铁凝固时通常会析出初生枝晶和晕圈枝晶,其形成条件主要与冷却速率和熔体的过冷有关.随铸件模数Mc增大,枝晶数量减少,二次臂间距显著增大,形态趋于不发达,由初生枝晶向晕圈枝晶过渡.当Mc≤0.3 cm时,二次臂间距的实测值与理论预测值基本吻合初生石墨球周围往往形成环状封闭奥氏体壳;共晶前期石墨球周围形成封闭或不封闭的框架奥氏体壳;共晶后期石墨球往往被周边生长着的共晶奥氏体所包覆,最终成为共晶奥氏体的一部分.
参考文献
| [1] | Loper C R, Heine R W, Reesman R W, Shah H. AFS Trans, 1967; 75:541 |
| [2] | Parks T W, Loper C R. AFS Trans, 1969; 77:90 |
| [3] | Wlodawar R. Gelenkte Erstarrung Von GuBeisen.GieBerei-Verlag: G.m.b.H., Dusseldorf, 1977:286 |
| [4] | Mulazimoglu M H, Yang Y M, Wallace J F, Ding N X,Mercer J L. AFS Trans, 1985; 93:627 |
| [5] | Zhou J Y, Xie Z H, Zhong F Q. Fundry, 1991; 3:9(周继扬,谢祖华,钟凤琪.铸造,1991;3:9) |
| [6] | Lux B, Mollard F, Minkoff I. Proc 2nd Int Symp on the Metallurgy of Cast Iron, Geneva, Switzerland, 1974:371 |
| [7] | Zhou J Y, Schmitz W, Engler S. AFS Trans, 1990; 23:783 |
| [8] | Xu J F, Yuan S, Wei B, Zai Q Y. Fundry, 1997; 11:17(徐锦锋,袁森,魏兵,翟秋亚铸造,1997;11:17) |
| [9] | Kurz W, Fisher D J. Fundamentals of Solidification.Switzerland: Trans Technol Publications Ltd, 1998:85 |
| [10] | Xu J F, Yuan S, Wei B, Zhai Q Y. J Xi'an Univ Technol,1998; (1): 94(徐锦锋,袁森,魏兵,翟秋亚.西安理工大学学报,1998;(1):94) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%