为了定量考虑热变形对普碳钢奥氏体向铁素体转变的影响,计算了热变形的C-Mn钢中的位错密度和变形储存能.在计算变形奥氏体向铁索体的平衡转变温度时,将计算所得变形储存能加在母相γ的能量项中,从而使变形奥氏体向铁素体转变的平衡转变温度Ae3提高,在本工作的热变形条件下,变形储存能为10-20 J/mol,使平衡转变温度Ae3提高10 K左右,因而相同的冷却条件下奥氏体向铁素体转变的实际温度Ar3也会提高.从γ/α界面移动速度控制铁素体生长速度角度的计算表明,奥氏体中储存能△Gdef使相变驱动力△Gγ→α增加,使铁素体的长大速度增加,加速奥氏体向铁素体的转变过程,但长大速度并未发生数量级的变化.在连续冷却相变模拟的过程中,利用超组元模型计算相变的平衡参数,计算结果与文献实验结果吻合良好.
参考文献
[1] | Tanaka T. Int Met Rev, 1981; 20:185 |
[2] | Zener C. J Appl Phys, 1949; 20:950 |
[3] | Enomoto M. Proc Int Conf on Physical Metallurgy of Thermo-Mechanical Processing of Steels and Other Metals (THERMEC 88), Tokyo: Iron Steel Inst Japan, 1988:360 |
[4] | Christian J W. The Theory of Transformations in Metals and Alloys. 2nd ed., Oxford: Pergamon Press, 1981:324 |
[5] | Krielaart G P, Sietsma J, van der Zwaag S. Mater Sci Eng, 1997; 237A:216 |
[6] | Agawal P K, Brimacombe J K. Metall Trans, 1981; 12B:121 |
[7] | de Ardo A J. In: Southwick P, ed., Proc Conf Accelerated Cooling of Steels, Pittsburgh, PA: AIME, 1986:97 |
[8] | Umemoto M, Hiramatsu A, Moriya A, Watamabe T,Nanba S, Nakajima N, Anan G, Higo Y. ISIJ Int, 1992;32:306 |
[9] | Liu X, Karjalainen L P, Pertulla J S. In: Beynon J H, Ingham P, Teichert H, Waterson K, eds., Proc 2nd Int Conf on Modeling of Metal Rolling Processes, London: The Institute of Metals, 1996:489 |
[10] | Crooks M J, Garrat-Peed A J, Vander Sande J B, Owen W S. Metall Trans, 1982; 13A: 1347 |
[11] | Torizuka S, Umezawa O, Tsuzaki K, Nagai K. Tetsu Hagané, 2000; 86:26(长尾彰英,仓本繁,菅野幹宏,白神哲夫.铁と钢,2000; 86: 26) |
[12] | Umenoto M, Ohtsuka H, Kato H, Tamura I. In: Dunne D P, Chandra T, eds., Proc Conf on High Strength Low Alloy Steels, Wollongong: University of Wollongong Press,1984:107 |
[13] | David H, Sietsma J, van der Zwaag S. ISIJ Int, 2001; 41:1028 |
[14] | Yoshie A, Fujita T, Fujioka M, Okamoto K, Morikawa H.ISIJ Int, 1996; 36:467 |
[15] | Yoshie A, Fujita T, Fujioka M, Okamoto K, Morikawa H.ISIJ Int, 1996; 36:474 |
[16] | Roters F, Raabe D, Gottstein G. Acta Mater, 2000; 48:4181 |
[17] | Luce R, Wolske M, Kopp R, Roters F, Gottstein G. Comput Mater Sci, 2001; 21:1 |
[18] | Aaronson H I, Domian H A, Pound G M. TMS AIME,1966; 236:768 |
[19] | Bhadeshia H K D H. Met Sci, 1981; 15:178 |
[20] | Clemm P J, Fisher J C. Acta Metall, 1955; 3:70 |
[21] | Qu J B. PhD Thesis, Northeastern University, Shenyang,1998:58(曲锦波.东北大学博士学位论文,沈阳,1998:58) |
[22] | Xu Z Y. The Theory of Phase Transformation, Beijing:Science Press, 2000:90(徐祖耀.相变原理,北京:科学出版社,2000:90) |
[23] | Kaufman L, Clougherty E V, Weiss R T. Acta Metall,1963; 11:323 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%