用电子显微镜观察了超级钢的熔化极混合气体保护脉冲焊三种焊接参数下的焊接接头粗晶区的精细结构,并测量了显微硬度沿焊缝的分布.结果表明:三种焊接参数下的热影响区中均未出现软化现象;随着热输入线能量的升高,粗晶区中的铁素体形态和碳化物的形态、分布和取向也变得复杂多样.在线能量低的接头粗晶区中,铁素体以块状为主,碳化物数量较少,呈粒状;在线能量较高的接头粗晶区中,铁素体以板条状为主,并在其上分布大量等轴状的亚单元,碳化物分布在亚单元的边界上或亚单元内部;在线能量高的接头粗晶区中,铁素体为板条状、块状,碳化物呈粒状,棒状等平行地分布在铁素体上,并与板条长轴呈不同的夹角.
参考文献
| [1] | Sato A. Proc Int Conf Ultra Steel 2000, Tsukuba, Japan,2000:1 |
| [2] | Niikura M, Fujioka M, Adachi Y, Matsakara A, Yokota T.J Mater Process, 2001; 117:341 |
| [3] | Worr P L. Development of High Performance Structural Steels for 21st Century in Korea. Tsukuba, Japan, 2000:179 |
| [4] | Peng Y, Wang C, Chen W Z, Tian Z L. Trans Chin Weld Inst, 2002; 22:32(彭云,王成,陈武柱,田志凌.焊接学报,2002;22:32) |
| [5] | Tian Z L, He C H, Zhang X M, Zou G, Qu Z X. Trans Chin Weld Inst, 2001; 22: 1(田志凌,何长红,张晓牧,邹钢,屈朝霞焊接学报,2001;22: 1) |
| [6] | Tian Z L. The Conference Document of Metal Weldability and Welding Materials Committee, Beijing, 2000(田志凌.金属焊接性与焊接材料委员会会议论文,北京,2000) |
| [7] | Qu Z X, Tian Z L, He C H, Zhang X M, Yang B, Cao N. Iron Steel, 2000; 35:70(屈朝霞,田志凌,何长红,张晓牧,杨柏,曹能.钢铁,2000; 35: 70) |
| [8] | Qu Z X. Ph D Thesis, Tianjin University, Tianjin, 2000(屈朝霞.天津大学博士学位论文,天津,2000) |
| [9] | Kang M K, Yang S P, Guan D H. Bainites in Steels.Shanghai: Shanghai Science and Technology Press, 1990:175(康沫狂,杨思品,管敦惠.钢中贝氏体.上海:上海科学技术出版社,1990:175 |
| [10] | Quidort D, Bre‘chet Y. Scr Mater, 2002; 47:151 |
| [11] | Fang H S, Yang J B, Yang Z G, Bai B Z. Scr Mater, 2002;47:157 |
| [12] | Van S, Wang J. Scr Mater, 2002; 47:163 |
| [13] | Hehemann R F. Phase Transformation. Metals Park, Ohio: ASM, 1968:397 |
| [14] | Yu D G. The Theory of Bainite Transformation. Shanghai: Shanghai Jiaotong University Press,1992:22(俞德刚.贝氏体相变理论.上海:上海交通大学出版社,1998:22) |
| [15] | Li F Z, Ao Q, Gu Y N, Jiang J, Sun D S. Acta Metall Sin,1997; 33:241(李凤照,敖青,顾英妮,姜江,孙东升.金属学报,1997;33:241) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%