运用电化学阻抗谱(EIS)和Fourier变换红外光谱研究了经过不同老化温度和老化时间处理的含锌铬黄防锈颜料的环氧酯漆在3.5%NaCl溶液中的阻抗谱特征,根据Fourier变换红外光谱和电化学阻抗谱中第二个时间常数出现的快慢及高频收缩情况来判断涂层的耐蚀性能,进而筛选老化工艺.结果表明,当老化温度为80℃和140℃,老化时间为3周时,涂层耐蚀性较好.其老化过程实际是有机高分子进一步发生交联反应和分子键破坏相互竞争的过程.同时提出了锌铬黄防锈颜料的作用机理.
参考文献
| [1] | Kendig M, Mansfeld F. Corrosion, 1983; 39:466 |
| [2] | Mansfeld F. Corrosion, 1988; 44:856 |
| [3] | Reinhard G, Rammelt V, Rammelt K. Corros Sci, 1986;26:109 |
| [4] | Skerry B S, Eden D A. Prog Org Coat, 1987; 15:269 |
| [5] | Rammelt U, Reinhard G. Prog Org Coat, 1992; 21:205 |
| [6] | Amirudin A, Thierry D. Prog Org Coat, 1995; 26:1 |
| [7] | Brett C M A. J Appl Electrochem, 1990; 20:1000 |
| [8] | Mansfeld F, Kendig M, Tsai S. Corrosion, 1982; 38:478 |
| [9] | Kendig M, Scully J. Corrosion, 1990; 46:22 |
| [10] | Kendig M, Mansfeld F, Tsai S. Corros Sci, 1983, 23:317 |
| [11] | Harhock M A, Lentz L A, Davis B L, Krishman K. Appll Spectrosc, 1986; 40:210 |
| [12] | Skrovanek D J. J Coat Technol, 1989; 61:31 |
| [13] | He D, Lei J Z, Hua X H. Aviation Paint and Coating Technol. Beijing: Chemical Industry Press, 2000:52(何鼎,雷骏志,华信浩.航空涂料与涂装技术.北京:化学工业出版社,2000:52) |
| [14] | Fang B Y, Han E H, Wang J Q, Zhu Z Y, Ke W, Hu J P, Xu Z G. Corros Sci Prot Technol, in press(方丙炎,韩恩厚,王俭秋,朱自勇,柯伟,胡建平,徐志刚.腐蚀科学与防护技术,待发表) |
| [15] | Zhu J L, Wu S N. Pigment Technological Skill. Beijing:Chemical Industry Press, 1989:252(朱骥良,吴申年.颜料工艺学.北京:化学工业出版社,1989:252) |
| [16] | Brasher M D, Kingsbury A H. J Appl Chem, 1954; 4:62 |
| [17] | Armstrong R D, Wright J D. Electrochim Acta, 1799; 38:1993 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%