提出了计算多元合金溶质分凝行为的热力学模型,分析了活度法和浓度法两种计算平衡分凝因数方法的异同.应用提出的模型系统地研究了Al-Cu-Zn合金的平衡分凝因数,计算表明,活度法和浓度法的计算结果接近,溶质Cu和Zn的平衡分凝因数在凝固温度范围内随温度增加下降10%左右,Zn和Cu任何一种溶质元素的浓度增加都会降低另一种元素的平衡分凝因数,同时研究了杂质元素对三元Al-Cu基合金中Cu的平衡分凝因数的影响.
参考文献
| [1] | Chen F Y, Jie W Q. Chin J Nonferrous Met, 2002; 12[A1 Special]: 85(陈福义,介万奇.中国有色金属学报,2002;12旧合金专辑]:85) |
| [2] | Sung P K, Poirier D R. Metall Mater Trans A, 1999; 30A: 2173 |
| [3] | Mao X M. PhD Dissertation, Northwestern Polytechnic University, Xi'an, 1981(毛协民.西北工业大学博士论文,西安,1981) |
| [4] | Roosz A, Szoke J, Rettenmayr M. Z Metallkd, 2000; 91: 1013 |
| [5] | Zhou G, Wang W H, Li Y Y. Acta Metall Sin, 2000; 36:472(周刚,王文皓,李依依.金属学报,2000;36:472) |
| [6] | Dinsdale A T. CALPHAD, 1991; 15:317 |
| [7] | Saunders N. COST 507 Round 1 Report: ThermochemicalDatabase for Light Metal Alloys. European Cooperation in the Field of Scientific and Technical Research, Euro pean Commission, 1994:19 |
| [8] | Kowalski M, Spencer P. J Phase Equil, 1993; 14:432 |
| [9] | Chen S L, Chang Y A. CALPHAD, 1993; 17:113 |
| [10] | Liang H, Chang Y A. J Phase Equil, 1999; 19:25 |
| [11] | Liu J J. PhD Dissertation, Northwestern Polytechnic Uni versity, Xi'an, 1987(刘家均.西北工业大学博士论文,西安,1987) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%