利用透射电子显微镜观察冷拔缩径变形和退火后低碳锰硼钢的组织形貌,研究了该钢的变形特征及组织演化规律.结果表明:在变形带中,铁索体沿平行于剪切应力方向形成条带状亚晶,{110}晶面为变形条带状亚晶的滑移面,条带状亚晶内存在高密度位错;经退火处理后,条带状亚晶内的位错束集成与条带状亚晶界垂直的位错胞壁,形成类方形位错胞结构;进一步经位错胞壁的扩散迁移,形成各胞壁之间虽120°夹角的亚品结构.
参考文献
[1] | Kuhlmann D, Wilsdorf H G F. Trans TMS-AIME, 1962;224:1047 |
[2] | Sestak B, Seeger A. Phys Status Solidi, 1971; 43:433 |
[3] | Sestak B, Seeger B. Z Metallkde, 1978; 69:355 |
[4] | Clauer AH, Wilcox B A, Hirth J P. Acta Metall Mater,1970; 18:381 |
[5] | Peeters B, Bacrolx B, Teodosiu C, Van Houtte P,Aernoudt E. Acta Mater, 2001; 49:1621 |
[6] | Andrade U, Meyers M A, Vecchio K S, Chokshi A H. Acta Metall Mater, 1994; 42:3183 |
[7] | Meyers M A, Han-Ryong Pek, Acta Metall, 1986; 34:2493 |
[8] | Meyers M A, Andrade U, Chokshi A H. Metall Mater Trans, 1995; 26A: 2881 |
[9] | Meyers M A, Chen Y J, Marquis F D S, Kim D S. Metall Mater Trans, 1995; 26A: 2494 |
[10] | Li Q, Xu Y B, Lai Z H, Shen L T, Bai Y L. Acta Metall Sin, 1999; 35:49(李强,徐永波,赖祖涵,沈乐天,白以龙.金属学报,1999;35:49) |
[11] | Meyers M A, Nesterenko V F, Lasalvia J C, Xu Y B, Xue Q. J Phys IV France, 2000; 10; 51 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%