用低频扭摆法测试了低掺杂La0.82Sr0.18MnO3巨磁电阻块材的内耗及弹性模量.所测试的温度范围内,在276和154 K存在两个内耗峰,且在相应的温度,模量有明显的变化.结合电磁性能的测试结果,认为高温峰起源于顺磁绝缘体斜方相向铁磁金属斜方相的转变.低温峰则被解释为铁磁金属斜方相向铁磁金属正方相的转变.
参考文献
| [1] | Li X G, Chen H, Zhu C F, Zhou H D, Zheng R K, Zhang J H. Appl Phys Lett, 2000; 76:1173 |
| [2] | Zhu C, Zheng R. Phys Rev, 1999; 59B: 11169 |
| [3] | Zhu C, Zheng R, Su J, He J. Appl Phys Lett, 1999; 74:3504 |
| [4] | Li K B, Li X J, Liu C S, Zhu Z G, Du J J, HouDL, Nie X F , Zhu J S, Zhang Y H. Phys Rev, 1997; 56B: 13662 |
| [5] | Zener C. Phys Rev, 1950; 81:440Zener C. Phys Rev, 1951; 82:403 |
| [6] | Zheng L Q, Fang Q F. J Phys: Condensed Matter, 2001;13:3411 |
| [7] | Ye S L, Song W H, Dai J M, Wang S G, Yuan C L, Sun Y P. J Appl Phys, 2000; 88:5915 |
| [8] | Zhang N, Zhang S, Ding W P, Zhong W, Du Y W. Solid State Commun, 1998; 107:417 |
| [9] | Steenbeck K, Eick T, Kirsch K, Schmidt H-G, Steinbei E.Appl Phys Lett, 1998; 73:2506 |
| [10] | Moritomo Y, Asamitsu A, Tokura Y. Phys Rev, 1997; 56B:12190 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%