用内耗的方法测量了钙钛矿结构锰氧化物La0 67Ca0 33MnO3的内耗温度曲线Q-1(T).在260,222和105 K温度处分别出现内耗峰.分析表明105 K处的内耗峰与铁磁态中的电子相分离有关.222 K处的内耗峰由两个次峰构成,峰温分别为222和234 K,并具有弛豫特征,与绝缘畴和金属畴的相对移动有关.它们的激活能以及指数前因子分别为0.32 eV,2.0×10-12s和0.38 eV,2.5×10-13 s.
参考文献
| [1] | Gammel L, Bishop D J, Zegarski B. Phys Rev Lett, 1996;76:3188 |
| [2] | Zener C. Phys Rev, 1951; 82:403 |
| [3] | Millis A J, Littlewood P B, Shraiman B I. Phys Rev Lett,1995; 74:5144 |
| [4] | Fath M, Freisem S, Menovsky A A, Tomioka Y, Aarts J,Mydosh J A. Science, 1999; 285:1540 |
| [5] | Heffner R H, Sonier J E, MacLaughlin D E, Nieuwenhuys G J, Ehlers G, Mezei F, Cheong S-W, Gardner J S, Roder H. Phys Rev Lett, 2000; 85:3285 |
| [6] | Du J J, Sun Y P, Jiang J Y, Zeng F C, Yin H Q. Phys Rev, 1990; 41 B: 6679 |
| [7] | Li K B, Li X, Liu C, Zhu Z, Du J, Hou D, Nie X, Zhu J,Zhang Y. Phys Rev, 1997; 56B: 13662 |
| [8] | Becker T, Streng C, Luo Y, Moshnyaga V, Damaschke B,Shannon N, Samwer K. Phys Rev Lett, 2002; 89:237203 |
| [9] | Savosta M M, Novák P. Phys Rev Lett, 2001; 87:137204 |
| [10] | Moreo A, Yunoki S, Dagotto E. Science, 1999; 283:2034 |
| [11] | Billinge S J L, Proffen Th, Petkov V, Sarrao J L, Kycia S. Phys Rev, 2000; 62B: 1203 |
| [12] | Yuan L X, Fang Q F. Acta Metall Sin, 1998; 34:1016(袁立曦,方前锋.金属学报,1998;34:1016) |
| [13] | Nowick A S, Berry B S. Anelastic Relaxation in Crystalline Solids. New York: Academic, 1972 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%