通过Gleeble-1500热力模拟实验机对仿晶界型铁素体/粒状贝氏体复相钢进行了Ar3以上不同温度、不同形变量的平面应变压缩实验.SEM和TEM观察表明,奥氏体形变不仅细化仿晶界型铁素体,而且促进先共析铁素体在原奥氏体晶内形核,从而有利于细化粒状贝氏体晶团及其内部的铁素体片条和MA岛.给出的组织变化模型可阐述形变对粒状贝氏体精细结构的影响.经过780℃下30%形变,即使在形变后空冷的条件下也获得了平均长度小于5 μm、平均宽度小于2.5 μm的仿晶界型铁素体晶粒、平均粒径小于3μm的晶内铁素体.与未经过形变的试样相比,CVN常温冲击韧性值从未形变的43 J提高到108 J,Vickers硬度从242提高到312,为工业生产工艺的改进提供了重要根据.
参考文献
| [1] | Hulka K, Hesterkamp F, Nachtel L. Processing, Microstructure and Properties of HSLA Steels. Warrendale,PA: TMS, 1988:153 |
| [2] | Czyryca E J. Key Eng Mater, 1993: 84-85:491 |
| [3] | Garcia C I, Lis A K, Pytel S M, DeArdo A J. ISS Transactions, 1992: 13:103 |
| [4] | Chiaki OUCHI. ISIJ International, 2001: 41(6): 542 |
| [5] | Fang H S, Xu P G, Bai B Z, Liu D Y. Heat Treat Met,2000: 11: 1(方鸿生,徐平光,白秉哲,刘东雨.金属热处理,2000:11:1) |
| [6] | Xu P G, Fang H S, Bai B Z, Wang Z J, Yang Z G, Huang J G. J Iron Steel Res Int, 2002: 9(2): 33 |
| [7] | Gibbs R K, Hodgson P D, Parker B A. In: Liaw P K ed,Morris E. Fine Symposium, Warrendale, PA: TMS, 1991:73 |
| [8] | Yada H, Matsumura Y, Senuma T. In: Tamura I ed,Proceedings of the International Conference on Physical Metallurgy of Thermomechanical Processing of Steels and Other metals, Tokyo: Iron and Steel Institute of Japan,1988:200 |
| [9] | Fang H S, Wang J J, Yang Z G, Li C M, Bo X Z, Zheng Y K. Bainite Transformation. Beijing: Science Press, 1999:11(方鸿生,王家军,杨志刚,李春明,薄祥正,郑燕康.贝氏体相变.科学出版社,1999:11) |
| [10] | Fang H S, Deng H J, Zhao R F, Zheng Y K. Mater Mech Eng, 1981: 5(1): 5(方鸿生,邓海金,赵如发,郑燕康.机械工程材料,1981:5(1):5) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%