用快速凝固/粉末冶金法,制备了致密超高强度块体Al90Mn8Ce2合金,其尺寸为直径20 mm、长10 mm.合金的致密度大于99%,合金抗压强度达到895 MPa,压延塑性超过6%.合金获得超高强度主要是由于亚稳态二十面体准晶相在803 K和1.2 GPa条件下仍稳定存在,对α-Al基体起强化作用.