采用区熔定向凝固方法,在30-720 mm/h生长速度范围内,均能获得〈110〉轴向择优取向生长的Tb-Dy-Fe合金;凝固形态随生长速度提高出现从平面晶到胞状晶、树枝晶转变;低速生长(30 mm/h)的样品磁致伸缩性能没有压力效应,高速生长(≥120 mm/h)的样品磁致伸缩性能具有明显的压力效应.低生长速度时〈110〉取向样品按双{111}系孪晶生长,高生长速度时按单{111}系孪晶生长,由此计算样品的磁致伸缩性能与实验结果基本吻合在更高生长速度下(900 mm/h)获得沿〈112〉轴向高度择优取向的样品,其磁致伸缩性能与高生长速度〈110〉取向样品性能相当,具有明显的压力效应.
参考文献
| [1] | Clark A E. Ferromagnetic Materials, Vol.1. Amsterdam:North-Holland, 1980:591 |
| [2] | Wu G H, Zhao X G, Wang J H, Li J Y, Jia K C, Zhan W S. Appl Phys Lett, 1995; 67:2005 |
| [3] | Mei W, Yoshizumi M, Okane T, Umeda T. J Alloys Compds, 1997; 258:34 |
| [4] | Verhoeven J D, Gibson E D, McMasters O D, Baker H H.Metall Trans A, 1987; 18:223 |
| [5] | Jiang C B, Zhou S Z, Zhang M C, Wang R. Acta Metall Sin, 1998; 34:164(蒋成保,周寿增,张茂才,王润.金属学报,1998;34:164) |
| [6] | Bonino O, Rango P D, Tournier R. J Magn Magn Mater,2000; 212:225 |
| [7] | Zhou S Z, Gao X X, Zhang M C, Zhao Q, Shi Z H. J Mater Sci Technol, 2000; 16:175 |
| [8] | Zhao Y, Jiang C B, Zhang H, Xu H B. J Alloys Compds,2003; 354:263 |
| [9] | Jiang C B, Zhou S Z, Xu H B, Wang R. Mater Sci Eng,1999; B58:191 |
| [10] | Jiang C B, Zhou S Z, Wang R. Chin Phys Lett, 1998; 15:379 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%