研究了元素Si对不同Nb含量TiAl合金抗氧化性能的影响.结果表明,合金中Nb含量越低,Si对合金抗氧化性能的提高作用越明显主要表现为Si促使二元合金形成连续致密的Al2O3层及使不同Nb含量合金表层氧化物更加均匀细小因而随Si含基的增加,TiAl合金的氧化增重速率系数降低,氧化速率下降.运用等温氧化增重实验、X射线衍射和扫描电镜等手段对Si的作用进行了分析讨论.
参考文献
[1] | Lipsitt H A. Mater Res Soc Symp Proc, 1985; 39:351 |
[2] | Kim Y W. JOM, 1989; 41:24 |
[3] | Yamaguchi M. Acta Mater, 2000; 48:307 |
[4] | Kim Y W. JOM, 1994; 46:30 |
[5] | Kim Y W. Acta Metall Mater, 1992; 40:1121 |
[6] | Liu C T, Schneibel J H, Maziasz P J, Wright J L, Easton D S. Intermetallics, 1996; 4:429 |
[7] | Brady M P, Brindley W J, Smialek J L, Locci I E. JOM,1996 48:46 |
[8] | Wang F, Lou H, Wu W. Oxid Met, 1995; 43:395 |
[9] | Bennett M J, Bull S J. Mater Corros, 1997; 48:48 |
[10] | Taniguchi S, Uesaki K, Zhu Y C, Zhang H X, Shibata T.Mater Sci Eng, 1998; A249:223 |
[11] | Shida Y, Anada H. Mater Trans JIM, 1994; 35:623-631 |
[12] | Chen G, Zhou X. Mater Sci Eng, 1992; A153:597 |
[13] | Zhang W, Chen G, Sun Z. Scr Metall Mater, 1993; 28:563 |
[14] | Becker S, Rahmel A, Schorr M, Schutze M. Oxid Met,1992; 38:425 |
[15] | Maki K, Shioda M, Sayashi M, Shimizu T, Isobe S. Mater Sci Eng, 1992; A153:591 |
[16] | Kim B G, Kim G M, Kim C J. Scr Metall Mater, 1995;30:1117 |
[17] | Tsuyama S, Mitao S, Minakawa K N. Mater Sci Eng, 1992;A153:451 |
[18] | Noda T. Intermetallics, 1998; 6:709 |
[19] | Nazmy M, Staubli M. US Patents 5, 286, 443(1994); 5,207, 982(1993); 5, 342, 577(1994) |
[20] | Yang R, Cui Y Y, Dong L M, Jia Q. J Mater Processing Technol, 2003; 135:179 |
[21] | Shida Y, Anada H. Corros Sci, 1993; 35:945 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%