分析了半固态金属制备过程中搅拌状态下晶粒生长的浓度场及温度场,将凝固速度与液体流动速度作为晶粒生长形态的影响因素,建立了液体运动状态下的晶粒生长形态模型,并且模拟了在不同半固态制备条件下晶粒的生长形态.理论模拟与实验结果相符合.
参考文献
[1] | Flemings M C. Metall Trans, 1991; 22A: 957 |
[2] | Kirkwood D K. Inter Mater Rev, 1994:173 |
[3] | Doherty R D, Lee H I, Feest E A. Mater Sci Eng, 1984;A65:181 |
[4] | Zhang J X, Zhang K, Liu G J, Xu J, Shi L K. The Chinese J Nonferrous Metals. 2000: 10:511(张景新,张奎,刘国钧,徐骏,石力开.中国有色金属学报,2000;10(4):511) |
[5] | Li T, Huang W D, Lin X. The Chinese J Nonferrous Metals, 2000; 10:635(李涛,黄卫东,林鑫.中国有色金属学报,2000;10(5):635) |
[6] | Wu S S,LiD N,Mao Y W,Song X J,Wu G Z,Luo J J.Foundry,2002;51:583(吴树森,李东南,毛有武,宋象军,吴广忠,罗吉荣铸造,2002;51:583) |
[7] | Perez M, Barbe J C, Neda Z, Brechet Y, Salvo L. Acta Mater, 2000; 48:3773 |
[8] | Niroumand B, Xia K. Mater Sci Eng, 2000; A283:70 |
[9] | Kurz W, Fisher D J. Fundamentals of Solidification.Switzerland: Trans Tech Publications LTD, 1986:163 |
[10] | Rappaz M, Thevoz P H. Acta Metall, 1987; 35:1487 |
[11] | Rappaz M, Thevoz P H. Acta Metall, 1987; 35:2929 |
[12] | Wu S S, Luo J J, Mao Y W, Song X J, Xiao Z H. Proc of the 7th Inter Conf on Semi-Solid Processing of Alloys and Composites, Tsukuba, Japan, 2002:843 |
[13] | Li D N, Luo J J, Wu S S, Xiao Z H, Mao Y W. J Mater Processing Technol, 2002; 129:431 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%