原始平均晶粒尺寸约为200μm的单相Ni-48Al金属间化合物在温度为1025-1100℃、应变速率为1.25×10-4-2.00×10-3s-1范围内呈现超塑性.在1100℃、应变速率为1.125×10-3.s-1时,最大延伸率可达188.2%.金相分析表明,超塑性变形过程中晶粒明显细化;电子背散射衍射分析(EBSD)和透射电子显微术(TEM)观察表明,超塑变形过程中形成了大量亚晶界网络,且随变形量增大,亚晶界及小角晶界比例不断增加.亚晶界由位错墙和位错网络构成,不稳定的亚晶界在超塑性变形过程中不断吸收晶内滑移和攀移位错,亚晶界位错密度不断增加,取向差不断增大.伴随亚晶界的滑移和迁移及亚晶的转动,部分亚晶界转变为小角度晶界,并进而转变为大角度晶界,即在超塑性变形过程中发生了连续动态回复与再结晶(CDRR).
参考文献
| [1] | Lin D L, Shan A D, Li D Q. Scr Metall Mater, 1994; 31:1455 |
| [2] | Li D Q, Shan A D, Liu Y, Lin D L. Scr Metall Mater,1995; 33:681 |
| [3] | Lin D L, Shan A D, Chen M W. Intermetallics, 1996; 4:489 |
| [4] | Lin D L, Li D Q, Liu Y. Intermetallics, 1998; 6:243 |
| [5] | Lin D L, Liu Y. Mater Sci Eng, 1999; A268:83 |
| [6] | Lin D L, Liu Y. Mater Sci Eng, 2002; A329:863 |
| [7] | Gu Y F, Lin D L, Shan A D, Chen J G, Hu F, Cao H Q.Acta Metall Sin, 1998; 34:351(谷月峰,林栋梁,单爱党,陈家光,胡凡,曹涵清.金属学报,1998;34:351) |
| [8] | Sun F, Lin D L. Scr Mater, 2001; 44:665 |
| [9] | Du X H, Guo J T, Zhou B D. Scr Mater, 2001; 45:69 |
| [10] | Jiang D, Lin D L. Mater Sci Lett, 2002; 21:505 |
| [11] | Jiang D, Lin D L. Mater Lett, 2002; 57:747 |
| [12] | Kim W-Y, Hanada S, Sakai T. Mater Sci Eng, 1998;A248:78 |
| [13] | Kogachi M, Hataguchi T. Mater Sci Eng, 2001; A312:189 |
| [14] | Liu Z Y, Lin D L, Chen D. Trans Nonferrous Met Soc Chin, 1997; 7:128 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%