研究了不同程度再结晶的Ni3Al(Zr)合金在真空和空气中的室温拉伸性能.结果表明,随着再结晶程度的增加,合金的塑性先增加后降低,不完全再结晶的样品表现出良好的拉伸塑性.合金的环境敏感指数随再结晶程度的增加而增加,完全再结晶的样品表现出强烈的环境敏感性.真空和空气中拉伸断口形貌的变化与力学性能变化趋势一致,再结晶程度低的样品的断口形貌为穿晶解理断裂,气氛对其几乎没有影响,而对再结晶程度高和完全再结晶的样品,空气使其沿晶断裂模式倾向增加.
参考文献
| [1] | Aoki K, Izumi O. J Jpn Inst Met, 1979; 43:1190(青木清,和泉修.日本金属学会志,1979;43:1190) |
| [2] | Mishima Y, Ochiai S, Hanao N, Yodogawa M, Suzuki T.Trans Jpn Inst Met, 1986; 27:656 |
| [3] | Hus S E, Hsu N S, Tong C H, Hu P H, Lee S Y, Ma J Y.Proc 1986 Annual Conf of The Chinese Society for Materials Science, Taizhong (Taichung), Taiwan, 1986:423 |
| [4] | Guo J T, Zheng Z, Sun C, Zhu Y X. In: Shi C X, Li H D, Scott A eds., The First Pacific Rim Int Conf on Advanced Materials and Processing, Warrendale, Pennsylvania: TMS, 1992:805 |
| [5] | George E P, Liu C T , Pope D P. Scr Metall Mater, 1992;27:365 |
| [6] | Su J Q, Gao S J, Yu B X, Guo J T. J Mater Sci, 1997;32:1201 |
| [7] | Yin W M, Guo J T, Hu Z Q. J Univ Sci and Technol Beijing, 1991; 13(Suppl.): 102(殷为民,郭建亭,胡壮麒.北京科技大学学报,1991;13(增刊):102) |
| [8] | Wan X J, Zhu J H, Huang S B. Acta Metall Sin, 1995; 31:B183(万晓景,朱家红,黄胜标.金属学报,1995;31:B183) |
| [9] | Liu C T, Oliver B F. J Mater Res, 1989; 4:294 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%