对名义成分为TiMn1.2-xCrxV0.25Fe0.05(x=0.0,0.1,0.2,0.3,0.4)合金的储氢性能进行了研究结果表明,合金的晶格常数和晶胞体积随Cr含量的增加而增大;随着Cr含量的增加,合金的吸/放氢平台压力和滞后效应减小.随着Cr含量的变化,TiMn1.2-xCrxV0.25Fe0.05合金112峰半高宽(FWHM)和晶格常数c/a比率的变化与该合金吸/放氢平台斜率的变化-致,表明合金的平台斜率与合金的晶格畸变关系密切.TiMn1.0Cr0.2V0.25Fe0.05合金具有较大的储氢量、低的平台压力、小的滞后和斜率,适于作为质子交换膜燃料电池供氢源的储氢瓶应用.
参考文献
[1] | Mani N, Sivakumar R, Ramaprabhu S. J Alloys Compd,2002; 337:148 |
[2] | Kim Jin-Ho, Lee Ho, Lee Paul S. J Alloys Compd, 2003;348:293 |
[3] | Tanaka K, Sowa M, Kita Y, Kubota T, Tanaka N. J Alloys Compd, 2002; 330-332:732 |
[4] | Lee Sang-Min, Yu Ji-Sang, Lee Ho, Jang Kulk-Jin, Lee Jai-Young. J Alloys Compd, 1999; 293-295:601 |
[5] | Mitrokhin S V, Bezuglaya T N, Verbetaky V N. J Alloys Compd, 2002; 330-332:146 |
[6] | Park Jeong-Gun, Jang Hwan-Young, Han Sang-Cheol,Lee Paul S, Lee Jai-Young. J Alloys Compd, 2001; 325:293-298 |
[7] | Hong C M, Hao D G, Lin Q Z. J Less-Common Met, 1991;172-174:1044 |
[8] | Mitrokhin S V, Verbetsky V N. J Alloys Compd, 1997;253-254:201 |
[9] | Hagstrom M T, Klyamkin S N, Lund P D. J Alloys Compd, 1999; 293-295:67 |
[10] | Guther V, Otto A. J Alloys Compd, 1999; 293-295:889 |
[11] | Yu X B , Wu Z, Huang T Z. Trans Nonferrous Met Soc Chin, 2003; 13:1116(余学斌,吴铸,黄太仲中国有色金属学报,2003;13:1116) |
[12] | Lundin C E, Lynch F E, Magee C B. J Less-Common Met, 1977; 56:19 |
[13] | Ivey D G, Northwood D O. J Mater Sci, 1981; 18:321 |
[14] | Park Jong-Man, Lee Jai-Young. J Less-Common Met,1991; 167:245 |
[15] | Magee C B, Lju J, Lundin C E. J Less-Common Met,1981; 78:119 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%