基于离散格点形式的微扩散方程(Langevin方程),对Al-Li合金在回归过程中δ′-Al3Li相溶解进行了原子层面计算机模拟,分析了析出相在回归过程中原子图像和序参数的演化,进而探讨了Al-Li合金的回归机制.首次探明Al-Li合金的回归过程有序相演化序列为化学计量比δ'相→非化学计量比有序相→无序基体,并论证了亚稳区合金的回归过程更趋向于失稳区合金时效过程的逆过程;失稳区合金的回归过程更趋向于亚稳区合金时效过程的逆过程.
参考文献
| [1] | Wang Z T.Mach Technol Light A11oys,1998;26:11(王祝堂.轻合金加工技术,1998;26:11) |
| [2] | Hassen P. Phase Transformations in Materials. Weinheim: VCH, 1991:281 |
| [3] | Cahn J W, Hilliard J E. J Chem Phys, 1958; 28:258 |
| [4] | Cahn J W, Hilliard J E. J Chem Phys, 1959; 31:688 |
| [5] | Chen L Q, Khachaturyan A G. Acta Metall Mater, 1991;39:2533 |
| [6] | Chen L Q, Khachaturyan A G. Phys Rev B, 1991; 44:4681 |
| [7] | hen L Q, Khachaturyan A G. Phys Rev B, 1992; 46:5899 |
| [8] | oduri R, Chen L Q. Acta Mater, 1996; 44:4253 |
| [9] | hen L Q, Khachaturyan A G. Scr Metall, 1991; 25:67 |
| [10] | i X L, Chen Z, Liu B, Wang Y X. Rare Met, 2001; 20:240 |
| [11] | Poduri R, Chen L Q. Acta Mater, 1997; 45:245 |
| [12] | Feng D. Metal Physics (Vol. 2). Beijing: Science Press,1998; 31:35(冯端.金属物理学(第二卷相变).北京:科学出版社,1998;31:35) |