利用电磁悬浮设备,通过在真空状态下反复加热与冷却处理,获得了Al50Si50(原子分数)合金熔体的深过冷,最大过冷度为320 K.观察了不同过冷度下凝固样品小球的表面及其截面深腐蚀后的组织形貌过冷度较小时,初生相Si为板条状枝晶形貌,并在其中发现了Al的层状沉积;过冷度较大时,初生相Si转变为粒状形貌.共晶体的形貌也随过冷度的增大转变为离异共晶形态.较大过冷度下,微观组织中发现有晶粒细化现象,这与Si晶体生长受溶质的抑制及初生相Si枝晶的断裂有关.
参考文献
[1] | Fredriksson H, Hillert M, Lange N. J Inst Met, 1973; 101:285 |
[2] | Hellawell A. Progress Mater Sci, 1970; 15:3 |
[3] | Smith R W. Modification of Aluminium-Silicon Alloys in the Solidification of Metals. London: Iron and Steel Inst,1968:1 |
[4] | Shamsuzzoha M, Hogan L M. Philos Mag A, 1986; 54:459 |
[5] | Zhang D L, Cantor B. Metall Trans A, 1993; 24:1195 |
[6] | Khan S, Elliot R. J Mater Sci, 1994; 29:736 |
[7] | Sens H, Eustathopoulos N, Camel D, Favier J J. Acta Metall Mater, 1992; 40:1783 |
[8] | Sundarrajan A, Mortensen A, Kattamis T Z, Flemings M C. Acta Metall Mater, 1998; 46:91 |
[9] | Magnin P, Mason J T, Trivedi R. Acta Metall Mater, 1991;39:469 |
[10] | Liang D, Bayraktar Y, Jones H. Acta Metall Mater, 1995;43:579 |
[11] | Ourdjini A, Elliot R. Mater Sci Technol, 1995; 11:1241 |
[12] | Bayraktar Y, Liang D, Jones H. J Mater Sci, 1995; 30:5939 |
[13] | Atasoy O A, Yilmaz F, Elliott R. J Cryst Growth, 1984;66:137 |
[14] | Pierantoni M, Gremaud M, Magnin P, Stoll D, Kurz W.Acta Metall Mater, 1992; 40:1637 |
[15] | Gremaud M, Allen D R, Perepezko J H. Acta Metall Mater, 1996; 44:2669 |
[16] | Allen D R, Gremaud M, Rappaz M, Perepezko J H. Mater Sci Eng A, 1997; 226:173 |
[17] | Lu S Z, Hellawell A. J Cryst Growth, 1985; 73:316 |
[18] | Wang R Y, Lu W H, Hogan L M. Metall Mater Trans A,1997; 28:1233 |
[19] | Apayadin N, Smith R W. Mater Sci Eng A, 1988; 98:149 |
[20] | Herlach D M, Cochrane R F, Egry I, Fecht H J, Greer A L. Int Mater Rev, 1993; 38:273 |
[21] | Devaud G, Turnbull D. Appl Phys Lett, 1985; 46:844 |
[22] | Liu R P, Volkmann T, Herlach D M. Acta Mater, 2001;49:439 |
[23] | Aoyama T, Takamura Y, Kuribayashi K. Metall Mater Trans A, 1999; 30:1333 |
[24] | Shao Y, Spaepen F. J Appl Phys, 1996; 79:2981 |
[25] | Evans P V, Vitta S, Hamerton R G, Greer A L, Turnbull D. Acta Metall Mater, 1990; 38:233 |
[26] | Lau C F, Kui H W. Acta Metall Mater, 1994; 42:3811 |
[27] | Trivedi R, Kurz W. Int Metall Rev, 1994; 39:49 |
[28] | Boettinger W J, Coriell S R, Trivedi R. In: Mehrabian R,Parrish P A eds., Rapid Solidification Processing: Principles and Technologies IV, Claitor's, Baton Rouge, L.A,1988:13 |
[29] | Li D, Herlach D M. Phys Rev Lett, 1996;. 77:1801 |
[30] | Battersby S E, Cochrane R F, Mullis A M. J Mater Sci,1999; 34:2049 |
[31] | Aoyama T, Kuribayashi K. Acta Mater, 2000; 48:3739 |
[32] | Macdonald C A, Malvezzi A M, Spaepen F. J Appl Phys,1989; 65:129 |
[33] | Aziz M J. J Appl Phys, 1982; 53:1158 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%