采用超高压电镜与离子加速器相连结的复合辐照装置,研究了注He对低活性Fe-Cr-Mn(W,V)合金辐照产生的点缺陷及二次缺陷行为的影响.实验结果表明:辐照初期形成的点缺陷与He相互作用,进而影响二次缺陷(位错、位错环和空洞)的形成;He明显促进位错密度增大和空洞核心形成,并导致空洞肿胀增加.对辐照产生的点缺陷与He相互作用的机理进行了理论分析.
参考文献
| [1] | Sizmann R. J Nucl Mater, 1968: 60-70:386 |
| [2] | Kojima S, Satoh Y, Ishida H. Philos Mag, 1989: 59A: 519 |
| [3] | Kojima S, Sano Y, Yoshiie T, Yoshida N. J Nucl Mater,1986: 141-143:571 |
| [4] | Takahashi H, Urbovn K. Phys Status Solidi, 1981: 16a:347 |
| [5] | Igata N, Kohno Y, Tsunakawa H, Fujihira T. ASTM STP 870, 1984:265 |
| [6] | Wilson W V, Baskes M I, Bisson C L. Phys Rev, 1976:13B: 2470 |
| [7] | Takahashi H, Takeyama T, Ohnuki S, Karo T. In: Takamura J, Doyama M, Kiritani M, eds., Point Defeats and Defect Interaction in Metals, New York: ASTM, 1982:861 |
| [8] | Zinkle S J, Wolfer W G, Seitzman L E. Philos Mag, 1987:55A: 127 |
| [9] | Bourret A. Phys Status Solidi, 1971: 6a: 813 |
| [10] | Urban K, Wilkens M. Phys Status Solidi, 1971: 6a: 173 |
| [11] | Egata N S. Materials of Fusion Reactors. Tokyo: Bafuean, 1986:131(井形直弘.核融合炉材料.东京:培风馆,1986:131) |
| [12] | Hu B F, Kinoshita H, Shibayama T, Takahashi H. Metall Mater Trans, 2002: 43:622 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%