利用原位X射线衍射及线形分析方法,测量加热过程中冷轧SiCw/Al复合材料基体晶块尺寸及显微畸变的变化规律,探讨复合材料再结晶行为.结果表明,复合材料基体晶粒长大及高温回复激活能均与纯Al自扩散激活能接近,证实了再结晶后晶粒长大伴随着高温回复现象,并且晶须对复合材料基体晶粒长大及高温回复的影响不明显.
参考文献
[1] | Lloyd D J. Int Mater Rev, 1994, 39(1): 1 |
[2] | Huda M D, Hashmi M S J, Ei-Baradie M A. Key Eng Mater, 1995, 104-107(Part Ⅰ): 37 |
[3] | Doherty R D, Hughes D A, Humphreys F J. Mater Sci Eng, 1997, A238:219 |
[4] | Clyne T W, Withers P J. An Introduction to Metal Matrix Composites. Cambridge: Cambridge University Press,1993:383 |
[5] | Liu Y L, Jensen D J, Hansen N. Metall Trans A, 1992,23A: 807 |
[6] | Teng F E, Wang Y M, Jiang X L. X-ray Structure Analysis and Property Representation of Materials. Beijing:Science Press, 1997:177(滕凤恩,王煜明,姜小龙.X射线结构分析与材料性能表征.北京:科学出版社,1997:177) |
[7] | Pan J S, Quan J M, Tian M B. Fundamentals of Materials Science. Beijing: Tsinghua University Press, 2002:513(潘金生,全健民,田民波.材料科学基础.北京:清华大学出版社,2002:513) |
[8] | Sherby O D, Burke P M. Prog Mater Sci, 1966: 13, 323 |
[9] | Jiang C H, Wang D Z, Yao C K. J Mater Sci Lett, 2000:19:1285 |
[10] | Jiang C H, Wu J S, Wang D Z. Trans Nonferrous Met Soc Chin, 2001: 11:729 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%