为了定量地描述多元合金的实际形核过程,引入实验参数,建立了工业多元合金凝固过程中的经验形核模型,该模型把形核率与最终晶粒密度联系起来.该模型能根据设计的参考试样的实验结果计算工业合金凝固过程中单位体积熔体中有效异质核心表面积Sv和熔体中有效异质核心润湿角因子f(θ),进而分析实际铸件的形核特性.利用所建立的经验形核模型,针对Al-7Si合金和Al-7Si-0.55Mg合金,计算了一定熔炼条件下的形核参数.
参考文献
| [1] | Turnbull D. J Appl Phys, 1950, 21:1022 |
| [2] | Turnbull D. J Chem Phys, 1950, 18:198 |
| [3] | Maxwell I, Hellawell A. Acta Metall, 1975, 23(2): 229 |
| [4] | Wei B B, Yang G C, Zhou Y H. Acta Mater, 1991, 39:1249 |
| [5] | Turbull D, Cech R E. J Appl Phys, 1950, 21:804 |
| [6] | Jian Z Y, Chang F E, Ma W H. Sci Chin, 2000, 43E(2):113 |
| [7] | Thompson C V, Spaepen F. Acta Metall, 1983, 31:2021 |
| [8] | Zhang X Z. Acta Mater, 1998, 46:1135 |
| [9] | Uolland-Moritz D, Schroess J, Herlach D M. Acta Mater,1998, 46:1601 |
| [10] | Rappaz M, Gandin C A. Acta Metall Mater, 1993, 41(2):345 |
| [11] | Thevoz Ph, Desbiolles J L, Rappaz M. Metall Mater Trans A, 1989, 20A: 311 |
| [12] | Christian J W. The Theory of Transformation in Metals and Alloys. Pergamon, Oxford, 1975:418 |
| [13] | Turnbull D. In: Seitz F, Turbull D eds, Solid State Physics. New York: Academic Press, 1956:225 |
| [14] | Spaepen F, Turnbull D. In: Grant N J, Giessen B C eds,Proc 2nd Int Conf On Rapidly Quenched Metals. Cambridge: MIT Press, 1976:205 |
| [15] | Spaaepen F. Acta Metall, 1975, 23:729 |
| [16] | Spaepen F, Meyer R B. Scr Metall, 1976, 10(1): 37 |
| [17] | Turnbull D. Contemporary Phys, 1969, 10:473 |
| [18] | Mueller B A, Perepezko J H. Metall Mater Trans A, 1987,18A: 1143 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%