通过对奥氏体再结晶行为的研究得到35CrMo钢发生动态再结晶的形变条件为:形变温度T＞1000℃,应变速率ε≤1/s.描述动态再结晶动力学方程f=1-exp(-b(Z)tn(Z))中的系数b和n与变形参数Z有关.计算值与实测值较为吻合.通过非线性回归得到35CrMo钢的动态再结晶晶粒尺寸的关系式为:DDRX=2.25×104Z-0.22.通过双道次压缩和单道次压缩保温实验,得出35CrMo钢静态再结晶激活能和动力学方程.
参考文献
| [1] | Sellars C M. Mater Sci Technol, 1990, 6:1072 |
| [2] | Mcqueen H J. J Mater Proc Technol, 1993, 37:3 |
| [3] | Mcqueen H J, Jonas J J. J Appl Metalworking, 1984, 3:233 |
| [4] | Wang G D, Liu Z Y. The Control Rolling and Control Cooling of HSLA Steel. Beijing: Metallurgy Industry Press, 1992:263(王国栋,刘振宇.高强度低合金钢的控制轧制与控制冷却.北京:冶金工业出版社,1992:263) |
| [5] | Weiss I, Sakai T, Jonas J J. Metall Sci, 1984, 2:77 |
| [6] | Laasraoui A, Jonas J J. Metall Trans A, 1991, 22A: 151 |
| [7] | Fabregue P. In: Jonas J J ed, Advances in Hot Deformation Texture and Microstructure. New York: The Materials Metals & Materials Society, 1994:75 |
| [8] | Dutta B, Sellars C M. Mater Sci Technol, 1987, 3:197 |
| [9] | Medina S F, Mancilla J E. ISIJ Int, 1996, 36:1070 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%