对孪晶铜进行塑性应变幅控制下的疲劳实验,研究了不同宽度的孪晶内疲劳位错组态及演化过程.结果表明,孪晶宽度不同时,孪晶内的疲劳位错组态不同.当孪晶宽度大于1 μm时,孪晶内疲劳位错组态与单晶中情况类似;孪晶宽度介于1 μm到200 nm之间时,位错形成类PSBs结构;孪晶宽度介于200 nm到20 nm之间时,孪晶内只能形成一些位错碎片;孪晶宽度小于20 nm时,孪晶内没有稳定的晶格位错存在.
参考文献
| [1] | Laird C, Charsley P, Mugurabi H. Mater Sci Eng, 1986,81:433 |
| [2] | Jia W P, Li S X, Wang Z G, Li X W, Li G Y. Acta Mater,1999, 47: 2165 |
| [3] | Feltner C E, Laird C. Aata Metall, 1967, 15:1633 |
| [4] | Vinogradov A, Kaneko Y, Kitagawa K, Hashimoto S, Stolyarov V, Valiev R. Scr Mater, 1997, 36:1345 |
| [5] | Witney A B, Sanders P G, Weertman J R, Eastman J A.Scr Metall Mater, 1995, 33:2025 |
| [6] | Lu L, Shen Y F, Chen X H, Qian L H, Lu K. Science,2004, 16:422 |
| [7] | Guo X L, Shen Y F, Lu L, Li S X. Aata Metall Sin, 2004;40:337(郭小龙, 申勇峰, 卢磊, 李守新. 金属学业报, 2004; 40: 337) |
| [8] | Wu S D, Wang Z G, Jiang C B, Li G Y, Alexandrov I V,Valiev R Z. Scr Mater, 2003, 48:1605 |
| [9] | Kawazoe H, Yoshida M, Basinski Z S, Niewczas M. Scr Mater, 1999, 40:639 |
| [10] | Konopka K, Mizera J, Wyrzykowski J W. J Mater Proc Technol, 2000, 99:255 |
| [11] | Neumann P. Fatigue. In: Cahn RW, Haasen P eds, Physical Metallurgy, Amsterdam: Elsevier Science, 1983:1554 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%