利用超声疲劳实验方法研究了2种商业42CrMo钢和2种零夹杂42CrMo钢在不同热处理制度下的超长寿命疲劳性能.结果表明,42CrMo钢疲劳S-N曲线在106-109cyc范围内无平台出现,疲劳极限消失;零夹杂42CrMo钢在此寿命区间有明显的疲劳极限.SEM断口观察表明,42CrMo试样疲劳开裂大多起源于非金属夹杂物,而零夹杂42CrMo全部起源于基体表面.零夹杂42CrMo钢的最大特点是在2×106-109cyc内不易发生疲劳断裂,疲劳寿命的可靠性显著增加.
参考文献
[1] | Fukumoto S, Mitchell A. Proceeding of the 1991 Vacuum Metallurgy Conference on the Melting and Processing of Specialty Materials I & SS, USA: Pittsburgh, 1991:3 |
[2] | Naito T, Ueda H, Kikuchi M. Met Trans, 1984; 15A: 1431 |
[3] | Asami K, Sugiyama Y. Heat Treatment Technol Assoc,1985; 25:147 |
[4] | Murakami Y. In: Blom A F ed., Proceedings of the 8th International Fatigue Congress, EMAS, Stockholm, Sweden, June, 2002:2927 |
[5] | Hu C T, Tarn C L. Mater Sci Eng, 1989; A118:25 |
[6] | Rittel D, Roman I. Iht J Fat, 1989; 111:177 |
[7] | Solberg J K. Mater Sci Eng, 1988; 101:39 |
[8] | Murakami Y. J Res Natl Inst Stand Technol, 1994; 99:345 |
[9] | Atkinson H V, Shi G. Prog Mater Sci, 2003; 48:457 |
[10] | Zhang J M, Zhang J F, Yang Z G, Li S X, Hui W J, Weng Y Q. Acta Metall Sin, 2004; 40:846(张继明,张建锋,杨振国,李守新,惠卫军,翁宇庆.金属学报,2004;40:846) |
[11] | Li S X. The Mechanical Behavior of Ultra-fine Grained Steel, The Ultra-fine Grained Steel, Beijing: Metallurgical Industry Press, 2003:891(李守新.超细晶钢的力学行为,超细晶钢.北京:冶金工业出版社,2003:891) |
[12] | Yang Z G, Zhang J M, Li S X, Chu Z M, Hui W J, Weng Y Q. Acta Metall Sin, 2004; 40:367(杨振国,张继明,李守新,褚作明,惠卫军,翁宇庆.金属学报,2004;40:367) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%