用SEM、TEM及XRD等方法研究了共析钢中珠光体经40%-90%的冷轧变形后所产生的显微组织变化.按渗碳体形态特点,变形珠光体组织可分为以下3种类型:(1)不规则弯曲片层型,即变形后的渗碳体与轧制面呈大角度偏离且不规则弯曲的珠光体.(2)带有剪切带的粗大片层型,即被渗碳体剪切带分开且变形轻微的珠光体.(3)精细片层型,即与轧制方向平行排列、片间距细小且渗碳体严重变形的珠光体.精细片层区域的比例随着轧制压下率的提高而增大.此外,重度冷轧变形还引起渗碳体严重塑性变形和部分溶解.
参考文献
| [1] | Weng Y Q. Ultra-Fine Grained Steels-Refining Theory and Controlling Technology for Microstructures in Steels.Beijing: Metallurgical Industry Press, 2003:4(翁宇庆.超细晶钢--钢的组织细化理论与控制技术,北京:冶金工业出版社,2003:4) |
| [2] | Takaki S, Maki T. Proc Int Symp on Ultrafine Grained Steels (ISUGS 2001), Tokyo: The ISIJ of Japan, 2001:1 |
| [3] | Maki T. Proc Workshop on New Generation Steel (NG STEEL '2001), Beijing: The Chinese Society for Metals,2001:27 |
| [4] | Fu W T, Furuhara T, Maki T. CAMP-ISIJ, 2001; 14:602 |
| [5] | Maki T. CAMP-ISIJ, 2001; 14:550 |
| [6] | Daitoh Y, Hamada T. Tetsu Hagane, 2000; 86:105(大藤善弘,浜田贵成.铁と钢,2000;86:105) |
| [7] | Sauvage X, Copreaux J, Danoix F, Blavette D. Philos Mag, 2000; 80A: 781 |
| [8] | Danoix F, Julien D, Sauvage X, Copreaux J. Mater Sci Eng, 1998; A250:8 |
| [9] | Langford G. Metall Trans, 1977; 8A: 861 |
| [10] | Takahashi T, Nagumo M, Asano Y. J Jpn Inst Met, 1978;42:708(高桥捻彦,南云道彦,浅野巌之.日本金属学会志,1978;42:708) |
| [11] | Fasiska E J, Wagenblast H. Trans TMS-AIME, 1967; 239:1818 |
| [12] | Nam W J, Bae C M, Oh S J, Kwon S J. Scr Mater, 2000;42:457 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%