研究了浸蚀对极化和未极化的BaTiO3单晶中畴变和压痕裂纹扩展的影响.结果表明,对面内极化试样(即极化方向[001],压痕面(100)),用HCl+HF水溶液浸蚀20 s,其压痕裂纹的平均长度由(140±17)μm扩展至(211±26)μm,即增长50%,同时压痕裂纹所围的90°畴变区也明显增大;先浸蚀再打压痕和压痕后再浸蚀所得的结果相同.其原因和浸蚀剂分子吸附降低表面能有关.对离面极化试样(即压痕面(001)垂直于极化方向[001]),则浸蚀对其裂纹长度和畴变区基本没有影响.对未极化试样,浸蚀使其裂纹长度从(150±21)μm增至(182±30)μm,即增长约20%,同时畴变区亦增大.
参考文献
| [1] | Busche M J, Hsia K J. Scr Mater, 2001; 44:207 |
| [2] | Fang F, Yang W. Mater Lett, 2002; 57:198 |
| [3] | Yang W. Mechatronic Reliability. Beijing: Tsinghua University Press, 2001:96(杨卫.力电失效学.北京:清华大学出版社,2001:96) |
| [4] | Geramita A V, Seberry J. Orthogonal Designs: Quadratic Forms and Hadamard Matrices. New York: Marcel Dekker, 1979 |
| [5] | Wang R M, Chu W Y, Gao K W, Su Y J, Qiao L J. Mater Lett, 2004; 58:1811 |
| [6] | Wang Y, Chu W Y , Su Y J, Qiao L J. Mater Sci Eng,2002; B59:263 |
| [7] | Chantikul P, Anstis G R, Lawn B R, Marshall D B. J Am Ceram Soc, 1981; 64:539 |
| [8] | Chu W Y, Qiao L J, Chen Q Z, Gao K W. Fracture and Environment Fracture. Beijing: Science Press, 2000:10(褚武扬,乔利杰,陈奇志,高克玮.断裂与环境断裂.北京:科学出版社,2000:10) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%