利用TGA,SEM/EDS研究了Ag含量对β-NiAl合金高温氧化时生成Al2O3膜表面形貌的影响及添加1%Ag(原子分数)对1000℃氧化动力学的影响.结果表明,β-NiAl合金的氧化动力学由两段抛物线组成,分别受亚稳Al2O3和稳态α-Al2O3的生长控制.NiAl-1Ag合金的氧化动力学由三段抛物线组成,分别受γ-Al2O3,θ-Al2O3和α-Al2O3的生长控制.1000℃时,向β-NiAl中添加少量的Ag(＜1%)可以促进亚稳Al2O3向稳态α-Al2O3的转变.当添加量超过5%时,促进作用不明显.1100℃时,添加0.5%Ag对Al2O3的相变无明显的促进作用.
参考文献
| [1] | Zhou J, Guo J T. Mater Sci Eng, 2003; A339:166 |
| [2] | Rybicki G C, Smialek J L. Oxid Met, 1989; 31:275 |
| [3] | Doychak J, Smialek J L, Mitchell T E. Metall Trans, 1989;20A: 499 |
| [4] | Mosely P T, Hyde K R, Bellany B A, Tappin G. Corros Sci, 1984; 24:547 |
| [5] | Doychak J, Ruhle M. Oxid Met, 1989; 31:431 |
| [6] | Hagel W C. Corrosion, 1965; 21:316 |
| [7] | Wood G C, Chattopadhay B. Corros Sci, 1970; 10:471 |
| [8] | Wood G C, Chattopadhay B. Oxid Met, 1970; 2:373 |
| [9] | Smialek J L, Gibala R. Metall Trans, 1983; A10:2143 |
| [10] | Brumm M W, Grabke H J. Corros Sci, 1992; 33:1677 |
| [11] | Brumm M W, Grabke H J. Corros Sci, 1993; 34:547 |
| [12] | Brumm M W, Grabke H J, Wagemann B. Corros Sci,1994; 36:37 |
| [13] | Grabke H J, Meier G H. Oxid Met, 1995; 44:147 |
| [14] | Grabke H J, Wiemer D, Viefhaus H. Appl Surf Sci, 1997;47:243 |
| [15] | Grabke H J, Brumm M W, Wagemann B. Mater Corros,1996; 47:675 |
| [16] | Pint B A, Treska M, Hobbs L W. Oxid Met, 1997; 47:1 |
| [17] | Yang S L, Wang F H, Niu Y, Wu W T. Mater Sci Forum,2001; 369-372:361 |
| [18] | Li M J, Sun X F, Guan H R, Jiang X X, Hu Z Q. Oxid Met, 2003; 59:483 |
| [19] | Li M J, Sun X F, Guan H R, Jiang X X, Hu Z Q. ActaMetall Sin, 2003; 39:755(李猛进,孙晓峰,管恒荣,姜晓霞,胡壮麒.金属学报,2003;39:755) |
| [20] | Zhang X J, Wu W T, Guo J T, Niu Y. High Temp Mater Proc, in press |
| [21] | Grabke H J. Intermetallics, 1999; 7:1153 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%