采用高压气体雾化技术制备了Cu-Fe合金粉末,并对粉末的组织进行了观察分析.结果表明,雾化液滴的尺寸与合金成分影响凝固组织的演变过程.雾化液滴尺寸越小,其内部富Fe相越弥散;Fe含量越接近亚稳液态组元不混溶区域的临界成分,越容易发生液-液相变.分析表明,富Fe液滴的Marangoni迁移和富Fe粒子与固-液界面之间的相互作用是导致粉末外部形成贫Fe层的主要原因.
参考文献
[1] | Spitzig W A. Acta Metall Mater, 1991; 39:1085 |
[2] | Li J F. Shanghai Met (Nonferrous Fasc), 1990; 11:18(李济富.上海金属,1990;11:18) |
[3] | Zhou W P,Lu D M.Rare Met Mater Eng,1993;22:24(周武平,吕大铭.稀有金属材料与工程,1993;22:41) |
[4] | Saxena S S, Tang J, Lee Y-S, O'Connor C J. J Appl Phys,1994; 76:6820 |
[5] | Elder S P, Munitz A, Abbaschian G J. Mater Sci Forum,1989; 50:137 |
[6] | Wilde G, Perepezko H J. Acta Mater, 1999; 47:3009 |
[7] | Biselli C, Morris D G. Acta Mater, 1996; 44:493 |
[8] | Nakagawa Y. Acta Metall, 1958; 6:704 |
[9] | Swartzendruber L J. In: Massalski T B, ed., Binary Alloy Phase Diagrams (2nd). New York: ASM, 1990:1409 |
[10] | Chuang Y-Y, Schmid R, Chang Y A. Metall Trans, 1984;15A: 1921 |
[11] | Chen Q, Jin Z P. Metall Mater Trans, 1995; 26A: 417 |
[12] | Wilde G, Willnecker R, Singh R N, Sommer F. Z Metallkd,1997; 88:804 |
[13] | Washizu T, Nagasaka T, Hino M. Z Metallkd, 2002; 93:281 |
[14] | Zhao J Z, Ratke L. Ser Mater, 2004; 50:543 |
[15] | Marangoni C. Ann Phys Chem, 1871; 143:337 |
[16] | Zubko A M, Lobanov V G, Nikonova V V. Soy Phys Crystallog, 1973; 18:239 |
[17] | Surappa M K, Rohatgi P K. J Mater Sci, 1981; 16:765 |
[18] | Pottlacher G. J Non-Cryst Solids, 1999; 251:177 |
[19] | Ye V, Zinovyev V F, Polev S G, Taluts G. Phys Met Metall, 1986; 61:85 |
[20] | Zinovev V E, Taluts S G, Kamashev M G, Vlasov B V,Polyakova V P. Phys Met Metall, 1994; 77:492 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%