利用能量120 keV的Al离子注入250和500℃的Fe靶,研究了高温注入条件下Fe靶表层合金化过程.Fe靶表层Al的浓度-深度分布和相结构分别采用Rutherford背散射谱(RBS)和X射线衍射谱(XRD)分析.实验结果表明:注入剂量为1×1017cm-2时,Al离子注入250和500℃Fe靶的注入深度分别为180和200 nm,峰值浓度均为10%(原子分数).离子注入层中形成了金属间化合物Al13Fe4相,同时记录到少量残留氧造成的氧化物AlFeO3相.利用有效形成热模型合理解释了Al离子高温注入Fe靶的合金相形成规律,利用相应金属离子高温注入金属靶传质模型可获得与实验相符的结果.
参考文献
| [1] | Huang P, Hochman R F. Mater Sci Eng, 1985; A115:257 |
| [2] | Lei M K, Zhang Z L. J Vac Sci Technol, 1995; 13A: 2986 |
| [3] | Williamson D L, Ozturk O, Wei R, Wilbur P J. Surf Coat Technol, 1994; 65:15 |
| [4] | Lei M K, Zhang Z L, Ma T C. Surf Coat Technol, 2000;131: 317 |
| [5] | Chang H W, Chen T, Lei M K. Acta Metall Sin, 2004; 40:629(常海威,陈涛,雷明凯.金属学报,2004;40:629) |
| [6] | Chang H W, Lei M K. Comput Mater Sci, to be published |
| [7] | Zhang T H, Ji C Z, Yang J H, Chen J, Shen J H, Lin W L, Gao Y Z, Sun G R. Surf Coat Technol, 1992; 51:455 |
| [8] | Miao W, Tao K, Liu X T, Liu B X. Surf Coat Technol,2001; 140:136 |
| [9] | Prudencio L M, da Silva R C, da Silva M F, Soares J C,Conde O, Vilar R. Surf Coat Technol, 2000; 128-129:166 |
| [10] | Pretorius R. Mater Res Soc Proc, 1984; 25:15 |
| [11] | Pretorius R, Vredenberg A M, Saris W J, de Reus R. J Appl Phys, 1991; 70:3636 |
| [12] | Zhang T H, Wu Y G, Zhang Y W, Qian W D. Vacuum,2002; 65:127 |
| [13] | Ji C Z, Zhang T H, Zhang H X, Xie J D, Wang A M.Radiat Eff Defects Solids, 1994; 129:161 |
| [14] | Miao W, Tao K, Liu B X, Li B. Nucl Instrum Meth, 2000;160B: 343 |
| [15] | Tu K N, Ottaviani G, Thompson R D, Mayer J W. J Appl Phys, 1985; 58:4125 |
| [16] | Liu B X, Gao K Y. Mater Chem Phys, 1998; 54:309 |
| [17] | Chang H W. M.S. Thesis, Dalian University of Technology, 2004(常海威.大连理工大学工学硕士学位论文,2004) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%