简要地总结了国内近年来在贝氏体相变理论研究方面的主要成果,包括以下方面:(1)发现钢中的贝氏体超精细结构;(2)贝氏体表面浮突完全由贝氏体铁素体长大过程中形变产生,单一超亚单元对应的浮突呈帐篷型;(3)贝氏体铁素体宽面上存在三维巨型台阶,在近N-W关系下相变单元宽面接近(335)f,为扩散型界面;(4)发现钢中贝氏体碳化物在α/γ界面的γ侧形核并向奥氏体内生长;(5)建立了贝氏体激发形核-台阶长大模型,理论计算表明这种机制是合理的,它成功地解释了贝氏体的多层次复杂结构,以及上贝氏体、下贝氏体等不同形态的形成原因等.
参考文献
[1] | Devenport E S, Bain E C. Trans Metall Soc AIME, 1930;90:117 |
[2] | Hillert M. Scr Mater, 2002; 47: 137; |
[3] | Hsu T Y, Mou Y W. Acta Metall, 1984; 32:1469 |
[4] | Mou Y W, Hsu T Y. Metall Trans, 1988; 19A: 1695 |
[5] | Hsu T Y. Metall Trans, 1990; 21A: 811 |
[6] | Kang M K, Yang S P, Guan D H. Bainite in Steel. Shanghai: Shanghai Scientific and Technical Publishers, 1990:57(康沫狂,杨思品,管敦惠.钢中贝氏体.上海:上海科学技术出版社,1990:57) |
[7] | Yu D G, Wang S D. Therory of the Bainite Transformation. Shanghai: Shanghai Jiaotong University Press,1998:79(俞德刚,王世道.贝氏体相变理论.上海:上海交通大学出版社,1998:79) |
[8] | Smith G V, Mehl R F. Trans AIME, 1942; 150:211 |
[9] | Aaronson H I, Wells C. JOM, 1956; 8:1216 |
[10] | Bhadeshia H K D H, Christian J W. Metall Trans, 1990;21A: 767 |
[11] | Fang H S, Wang J J, Yang Z G. Prog Nat Sci, 1993; 3:525(方鸿生,王家军,杨志刚.自然科学进展,1993;3:525) |
[12] | Fang H S, Wang J J, Yang Z G, Li C M, Bo X Z, Zheng Y K. Bainite Transformation. Beijing: Science Press, 1999:512(方鸿生,王家军,杨志刚,李春明,薄祥正,郑燕康.贝氏体相变.北京:科学技术出版社,1999:512) |
[13] | Ko T, Cottrell S A. Iron Steel Inst, 1952; 172:307 |
[14] | Bo X Z, Fang H S, Wang J J. Mater Trans JIM, 1997; 38:965 |
[15] | Swallow E, Bhadeshia H K D H. Mater Sci Technol, 1996;12:121 |
[16] | Fang H S, Wang J J, Zheng Y K. Metall Mater Trans,1994; 25A: 2001 |
[17] | Srinivasan G R, Wayman C M. Acta Metall, 1968; 16:621 |
[18] | Srinivasan G R, Wayman C M. Acta Metall, 1968; 16:609 |
[19] | Hall M G, Rigsbee J M, Aaronson H I. Acta Metall, 1986;34:1419 |
[20] | Weatherly G C, Zhang W Z. Metall Mater Trans, 1994;25A: 1865 |
[21] | Aaronson H I, Hall M G. Metall Mater Trans, 1994; 25A:1797 |
[22] | Fang H S, Wang J J, Deng Y K, Yang Z G. Acta Metall Sin, 1993; 29A: 445(方鸿生,王家军,郑燕康,杨志刚.金属学报,1993;29A:445) |
[23] | Fang H S, Bo X Z, Wang J J. Mater Trans JIM, 1998; 39:1264 |
[24] | Yang Z G, Zhang C, Fang H S, Yang J B, Bai B Z, Wang J J. J Mater Sci Technol, 2001; 17:433 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%