热模拟单向压缩下中碳钢形变温度低于Ad3(786℃)点时,析出形变诱导铁素体(DIF),DIF量随形变温度降低而提高;在低于750℃形变时,DIF量远高于平衡态铁素体含量54%.DIF析出时碳原子高度富集在铁素体晶界和铁素体/奥氏体界面.在低于A1(719℃)等温处理时,高于Ad3点形变试样中,奥氏体转变为铁素体+片层状珠光体;低于Ad3点但高于Ar3(645℃)点形变时,未转变奥氏体转变为铁素体+片层状珠光体+晶界渗碳体;稍高于Ar3点形变时,将获得铁素体+弥散渗碳体的球化组织.
参考文献
[1] | Weng Y Q. Iron Steel, 2003; 38(5): 1(翁宇庆.钢铁,2003;38(5);1) |
[2] | Tsuji N. Tetsu Hagane, 2002; 88:359(辻伸泰.铁と钢,2002;88:359) |
[3] | Li W J, Wang G D, Liu X H. In: Workshop on New Generation Steel (NG Steel'2001), Beijing: The Chinese Society for Metals, 2001:311(李维娟,王国栋,刘相华.见:新一代钢铁材料研讨会,北京,中国金属学会,2001:311) |
[4] | Tian Z X, Yang P, Sun Z Q. Trans Mater Heat Treat,2003; 24(3): 18(田朝旭,杨平,孙祖庆.材料热处理学报,2003;24(3):18) |
[5] | O'Brien J M, Hosford W F. Metall Mater Trans, 2002;33A: 1255 |
[6] | Park J, Song D H, Lee D, Choo W Y. In: Zhu Y T, Langdon T G, Mishra R S, Semiatin S L, Saran M J, Lowe T C, eds., Ultrafine Grained Materials Ⅱ, Seattle: The Minerals, Metals & Materials Society, 2002:275 |
[7] | Storojeva L, Kaspar R, Ponge D. Mater Sci Forum, 2003;426-432:1169 |
[8] | Weng Y Q, et al. Ultrafine Grained Steels-The Theory of Microstructure Refinement and Controlling Technology for Steels. Beijing: Metallurgical Industry Press, 2003:140, 118(翁宇庆,等.超细晶钢--钢的组织细化理论与控制技术.北京:冶金工业出版社,2003:140,118) |
[9] | McQueen H J, Ryan N D. Mater Sci Eng, 2002; A322:43 |
[10] | An Y Z. Heat Treatment Technology. Beijing: China Machine Press, 1982:51(安运铮.热处理工艺学.北京:机械工业出版社,1982:51) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%