研究了带环状预裂纹不锈钢圆棒试样在循环扭转载荷下、门槛值附近的疲劳裂纹扩展行为,用应力强度因子表征了裂纹扩展开始的门槛值.随着裂纹的扩展,裂纹扩展速率由于裂纹面的滑移接触而减小.通过外插裂纹扩展速率与裂纹长度之间的关系,可近似得到裂纹长度为零时无裂纹面滑移接触影响的裂纹扩展速率.施加的应力强度因子范围可分解为推动裂纹扩展的有效值和由于裂纹面的滑移接触而屏蔽掉的两部分.预测了疲劳裂纹的萌生和断裂极限,预测值和实验值相当一致.
参考文献
| [1] | Pook L P. Int J Fatigue, 1985; 7(1): 21 |
| [2] | Yates J R, Miller K J. Fatigue Fract Eng Mater Struct,1989; 12:259 |
| [3] | Yoshioka S, Watanabe K, Kitagawa H, Inoue A, Kumasawa M. Trans Jpn Soci Mech Eng, 1984; 50(453): 1267 |
| [4] | Tschegg E K. Mater Sci Eng, 1982; 54:127 |
| [5] | Tschegg E K. J Mater Sci, 1983; 18:1604 |
| [6] | Yu H C, Tanaka K, Akiniwa Y. Fatigue Fract Eng Mater Struct, 1998; 21:1067 |
| [7] | Yu H C, Xie S S, Tanaka K, Akiniwa Y. J Mater Eng,2002; (Suppl.): 317(于慧臣,谢世殊,田中启介,秋庭义明.材料工程,2002;(增刊):317) |
| [8] | Yu H C, Xie S S, Sun Y G, Tanaka K. J Aeronaut Mater,2004; 24(5): 53(于慧臣,谢世殊,孙燕国,田中启介.航空材料学报,2004;24(5):53) |
| [9] | Yu H C, Sun Y G, Xie S S, Tanaka K. Acta Metall Sin,2005; 41:73(于慧臣,孙燕国,谢世殊,田中启介.金属学报,2005;41:73) |
| [10] | Ritchie R O, McClintock F A, Hayeb-Hashemi H, Ritter M A. Metall Trans, 1982; 13A: 101 |
| [11] | Tada H, Paris P C, Irwin G R. The Stress Intensity Factor Handbook. 2nd ed., 1985:27 |
| [12] | Tanaka K, Akiniwa Y, Nakamura H. Fatigue Fract Eng Mater Struct, 1996; 19:571 |
| [13] | Tanaka K, Akiniwa Y, Yu H C. ASTM STP 1359, 1999:295 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%