利用电弧熔炼及铜模快速铸造的方法制备Zr41.2Ti13.8Cu12.5Ni10Be22.5块状非晶合金,通过电化学方法向块状非晶中充入氢.结果表明,氢提高玻璃转变温度下的线膨胀系数,降低晶化开始温度处的线膨胀系数,延缓玻璃转变前结构弛豫现象的发生.另外,充氢能够增加块体非晶合金材料的原子平均最近邻距离和有效作用势深度.
参考文献
| [1] | Kǒster U, Zander D. Mater Sci Forum, 2000; 343-346:203 |
| [2] | Suh D, Dauskardt R H. Scr Mater, 2000; 42:233 |
| [3] | Zander D, Leptien H, Kǒster U, Eliaz N, Eliezer D. J Non-Cryst Solids, 1999; 250-252:893 |
| [4] | Peng D L, Shen J, Sun J F, Chen Y Y. Acta Metall Sin,2003; 39:1081(彭德林,沈军,孙剑飞,陈玉勇.金属学报,2003;39:1081) |
| [5] | Peng D L, Shen J, Sun J F, Chen D M, Chen Y Y. Chin J Nonferrous Met, 2003; 13:846(彭德林,沈军,孙剑飞,陈德民,陈玉勇.中国有色金属学报,2003;13:846) |
| [6] | Peng D L, Shen J, Sun J F, Chen Y Y. J Mater Sci Technol, 2004; 20:157 |
| [7] | Chen C L. Solid Physics. Xi'an: Northwestern Polytechnical University Press, 2000:37(陈长乐.固体物理学.西安:西北工业大学出版社,2000:37) |
| [8] | Porscha B, Neuhauser H. Phys Status Solidi, 1994; 186B:119 |
| [9] | Fu L. Met Funct Mater, 1998; 5:39(富莉.金属功能材料,1998;5:39) |
| [10] | Jing Q, Liu R P, Li G, Wang W K. Scr Mater, 2003; 49:111 |
| [11] | Wang H W, Wei Q, Friedrich S. J Phys Rev, 1998; 57B:8211 |
| [12] | Lu I R, Gorler G P, Fecht H J, Willnecker R. J Non-Cryst Solids, 2000; 274:294 |
| [13] | Yu B, Chen W J, Zheng G Z, Lin G M. Acta Sci Nat Univ Sunyatseni, 2001; 40:120(余斌,陈文军,郑国祯,林光明.中山大学学报(自然科学版),2001;40:120) |
| [14] | Suh D, Dauskardt R H. Scr Mater, 2000; 42:233 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%