采用高功率直流电弧等离子体CVD工艺制备了不同厚度的无裂纹自支撑金刚石厚膜.实验中观察到在金刚石厚膜生长过程中出现了形貌不稳定性,其程度随甲烷浓度的不同而变化.从理论和实验两个方面对这种不稳定性进行了讨论,认为直流电弧等离子体的高温造成碳源高饱和度是生长不稳定性的根本原因.实验结果表明,在沉积金刚石厚膜时,为了稳定地获得高质量的厚膜,甲烷浓度不宜过高.
参考文献
| [1] | Busch J V, Dismukes J P. Diamond Relat Mater, 1994; 3:295 |
| [2] | Lü F X, Huang T B, Tang W Z, Song J H, Tong Y M.Trans Mater Heat Treat, 2001; 22(1): 46(吕反修,黄天斌,唐伟忠,宋建华,佟玉梅.材料热处理学报,2001;22(1):46) |
| [3] | Ravi K V. J Mater Res, 1992; 7:384 |
| [4] | Lu F X, Zhong G F, Sun J G, Fu Y L, Tang W Z, Wang J J, Li G H, Zang J M, Pan C H, Tang C H, Lo T L, Zhang Y G. Diamond Relat Mater, 1998; 7:737 |
| [5] | Lu F X, Tang W Z, Huang T B, Liu J M, Song J H, Yu W X, Tong Y M. Diamond Relat Mater, 2001; 10:1551 |
| [6] | Zuo D W, Song S L, Wang M. Key Engin Mater, 2004;258-259:517 |
| [7] | Lu W Z, Zuo D W, Wang M, Li X F, Song S L, Xiang B K. Mach Design Manuf, 2003; 41(6): 81(卢文壮,左敦稳,王珉,黎向锋,宋胜利,相炳坤.机械设计与制造,2003;41(6):81) |
| [8] | Goodwin D G. J Appl Phys, 1993; 74:6890 |
| [9] | Song S L, Zuo D W, Wang M, Li X F. J Appl Sci, 2003;21:423(宋胜利,左敦稳,王珉,黎向锋.应用科学学报,2003;21:423) |
| [10] | Zhu Y, Zuo D W, Wang M, Lu W Z, Song S L. J Synth Crys, 2003; 32:605(朱胤,左敦稳,王珉,卢文壮,宋胜利.人工晶体学报,2003;32:605) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%