采用XRD,SEM,TEM和光激发荧光谱等技术对电弧离子镀制备的NiCoCrAlY涂层的组织结构和初期氧化的机理进行了研究.结果表明,电弧离子镀方法沉积的NiCoCrAlY涂层具有纳米晶体结构,呈明显的层状生长真空退火后涂层内的层状结构消失,涂层组织更致密,晶粒明显长大,有孪晶出现.涂层在真空退火后表面已经生成一层很薄的以α-Al2O3为主的氧化膜,在高温氧化过程中,涂层表面的亚稳态氧化物θ-Al2O3先增多,然后逐渐转变为稳态的α-Al2O3,并对其相关机理进行了探讨.
参考文献
| [1] | Padture N P, Gell M, Jordan E H. Science, 2002; 296:280 |
| [2] | Nicholls J R. MRS Bull, 2003:659 |
| [3] | Knotek O, Loffler F, Beele W. Surf Coat Technol, 1993;61:6 |
| [4] | Wang Q M, Wu Y N, Guo M H, Ke P L, Gong J, Sun C,Wen L S. Surf Coat Technol, 2005; 197:68 |
| [5] | Nicholls J R, Simms N J, Chan W Y, Evans H E. Surf Coat Technol, 2002; 149:236 |
| [6] | Guo M H, Wang Q M, Ke P L, Gong J, Sun C, Huang R F, Wen L S. Surf Coat Technol, in press |
| [7] | Wang F H, Lou H Y, Wu W T. Corros Sci Prot Technol,1992; 4:156(王福会,楼翰一,吴维[].腐蚀科学与防护技术,1992;4:156) |
| [8] | Wang B, Song G H, Gong J, Sun C, Wen L S, Ham Y F.Oxid Met, 2001; 56:1 |
| [9] | Wang Q M, Wu Y N, Ke P L, Gao H T, Gong J, Sun C,Wen L S. Surf Coat Technol, 2004; 186:389 |
| [10] | Wu Y N, Wang Q M, Ke P L, Sun C, Gong J, Wang F H,Wen L S. Surf Coat Technol, in press |
| [11] | Wang F H, Lou H Y, Li M S, Wu W T. Corros Sci Prot Technol, 1994; 6:7(王福会,楼翰一,李美栓,吴维(山女).腐蚀科学与防护技术,1994;6:7) |
| [12] | Brandl W, Toma D, Grabke H J. Surf Coat Technol, 1998;108/109:10 |
| [13] | Wu Y N, Hua W G, Ji A L, Wang F H, Sun C, Wen L S.Acta Metall Sin, 2002; 38:1082(武颖娜,华伟刚,纪爱玲,王福会,孙超,闻立时.金属学报,2002;38:1082) |
| [14] | Choquet P, Mevrel R. Mater Sci Eng, 1989; A120:153 |
| [15] | Peng X, Wang F H, Clarke D R. Acta Metall Sin, 2003;39:1055(彭晓,王福会,Clarke D R.金属学报,2003;39:1055) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%