通过考虑相图计算公式中基本参数--熔化温度和熔化焓的尺寸效应与形状效应,研究了完全互溶的二元纳米金属微粒系统理想溶液的相图研究结果表明,纳米微粒的相图也依赖于微粒的尺寸和形状因子.对Cr-Mo纳米微粒系统相图的计算结果表明,纳米微粒相图的固相线和液相线要比相应块体材料的固相线和液相线低,但与已报道的结果不同的是,固、液相线变化的幅度基本相同.这与本文目前不仅考虑了纳米微粒熔化温度的影响,还考虑了纳米微粒熔化焓的影响有关.
参考文献
| [1] | Wautelet M,Dauchot J P,Hecq M.Mater Sci Eng,2003;C23:187 |
| [2] | Wautelet M,Dauchot J P,Hecq M.Nanotechnology,2000;11:6 |
| [3] | Lai S L,Guo J Y,Petrova V.Phys Rev Lett,1996; 77:99 |
| [4] | Eckert J,Holzer J C,Ahn C C,Fu Z,Johnson W L.Nanostruct Mater,1993,2:407 |
| [5] | Jiang Q,Yang C C,Li J C.Mater Lett,2002; 56:1019 |
| [6] | Xu ZY,Li L.Thermodynamics of Material.Beijing:Science Press,2001:148(徐祖耀,李麟.材料热力学.北京:科学出版社,2001:148) |
| [7] | Qi W H,Wang M P.Chem Phys Lett,2003; 372:632 |
| [8] | Qi W H,Wang M P.Mater Chem Phys,2004; 88:280 |
| [9] | Kim H K,Huh S H,Park J W,Jeong J W,Lee G H.Chem Phys Lett,2002; 354:165 |
| [10] | Rose J H,Ferrante J,Smith J R.Phys Rev Lett,1981; 47:675 |
| [11] | Mott N F.Proc Roy Soc Lond,1934; 146A:465 |
| [12] | Regel A R,Glazov V M.Semiconductors,1995; 29:405 |
| [13] | Ubbelohde A R.Melting and Crystal Structure.Oxford:Clarendon Press,1965:88 |
| [14] | Zhang Z ,Lu X X,Jiang Q.Physica,1999; B270:249 |
| [15] | Hou Z S,Lu G X.Principle of Metallography.Shanghai:Shanghai Technology and Science Press,1990:63(侯增寿,卢光熙.金属学原理.上海:上海科学技术出版社,1990:63) |
| [16] | Nanda K K,Sahu S N,Behera S N.Phys Rev,2002; 66A:013208 |
| [17] | Brandes E A.Smithells Metals Rreference Book.6th ed.London:Butterworths,1983:8 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%