硼酸铝晶须增强铝复合材料中加入Fe3O4颗粒可以降低该复合材料的热膨胀系数.研究认为复合材料中Fe3O4颗粒在制备过程中部分被氧化,在热膨胀测试过程中被氧化的Fe3O4又被还原,其体积将变小,基体铝的膨胀受到限制,相当于具有负膨胀系数性质,从而起到了降低复合材料热膨胀系数的作用.结合复合材料中Fe3O4磁场热重曲线分析,阐述了颗粒的残余应力在热循环中的变化情况.
参考文献
| [1] | Arsenault R J,Taya M.Acta Metall,1987; 35:651 |
| [2] | Arsenault R J,Wu S B.Mater Sci Eng,1987; 96:77 |
| [3] | Fei W D,Hu M,Yao C K.Mater Chem Phys,2003; 77:882 |
| [4] | Fei W D,Chu W G,Yang W,Liu Q Y,Yao C K.Mater Sci Technol,2000; 16:431 |
| [5] | Fei W D,Liu Q Y,Liang N G,Yao C K.Mater Sci Technol,2001; 17:912 |
| [6] | Li G,Sun Y,Fei W D.Mater Lett,2003; 57:3217 |
| [7] | Levy D,Artioli G,Dapiaggi M.J Solid State Chem,2004;177:1713 |
| [8] | Wang L D,Fei W D,Jiang L S,Yao C K.J Mater Sci Lett,2002; 21:737 |
| [9] | Kim C T,Lee J K,Plichta M R.Metall Trans,1990; 21A:673 |
| [10] | Maeda K,Wakashima K,Ono M.Scr Mater,1997; 36:335 |
| [11] | Samara G A,Giardini A A.Phys Rev,1969; 186:577 |
| [12] | Govindarajan R,Carmichael C M,Schloessin H H.Phys Earth Plan Int,1982; 29:108 |
| [13] | Jiang S T,Li W.Magnetic Physics of Condensed State(2nd,ed).Beijing:Science Press,2005:55(姜寿亭,李卫.凝聚态磁性物理(第二版).北京:科学出版社,2005:55) |
| [14] | Chaianni A,Yokoya T,Morimoto T,Takahashi T,Todo S.J Electron Spectros Relat Phenom,1996; 78:99 |
| [15] | Li Y R,Yun Z Z.An Introduction to Electronic Materials.Beijing:Tsinghua University Press,2001:329(李言荣,恽正中.电子材料导论.北京:清华大学出版社,2001:329) |
| [16] | Fei W D,Wang L D.Mater Chem Phys,2004;85:450 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%