以TiO2和PbC2O4为反应物,NaCl和NaCl-KCl为熔剂,于820-1000℃保温2 h制备了纯净的PbTiO3粉体.熔盐法制备过程中盐的用量以及温度明显的影响晶粒的尺寸,当温度低于900℃时,在氯化物盐中随着温度的升高,晶粒尺寸逐渐增大;当温度高于900℃时,晶粒尺寸随温度的升高变化不大,晶粒最终发育为较完整的球形.熔盐合成晶体生长过程为扩散机制控制,通过调整熔盐的用量及温度可以控制晶粒的尺寸与形貌.熔盐法制备PbTiO3粉体工艺流程简单,时间短,产量大,成本低,无污染.
参考文献
| [1] | Gao F,Yang Z P,Liu X C,Tian C S.Acta Mater Com Sin,2004; 21(5):22(高峰,杨祖培,刘向春,田长生.复合材料学报,2004;21(5):22) |
| [2] | Chen Y H,Zhu C G,Wei Y J,Chu D B.Chin J Inorg Chem,2004;21:1121(陈永红,朱传高,魏亦军,褚道葆.无机化学学报.2004;20:1121) |
| [3] | Dowson W J.Am Ceram Soc Bull,1988,67:1673 |
| [4] | Xing X R,Deng J X,Chen J.Rare Met.2003; 22 :294 |
| [5] | Calzada M L,Mendiola J,Carmona F,Ramos P,Sirera R.Mater Res Bull,1996; 31:413 |
| [6] | Sani A,Hanfland M,Levy D.J Solid Chem,2002; 167:446 |
| [7] | Arendt R H.J Solid State Chem,1973; 8:339 |
| [8] | Fiorino M E.J Powder Sources,1997; 66:177 |
| [9] | Idrissi H,Aboujalil A,Deloume J P,Fantozzi G,Durand B.J Eur Ceram Soc,1999; 19:1997 |
| [10] | Ito Y,Shimada S,Takahashi J I.J Mater Chem,1997; 7:781 |
| [11] | Mao Y B,Banerjee S,Wong S S.J Am Chem Soc,2003;125:15718 |
| [12] | Wan D M,Wang J,Ng S J.J Alloy Compd,1998; 274:110 |
| [13] | Liu H X,Sun X Q,Xiao J,Cheng Z Z,Zhou J,Ouyang S X.Acta Chem Sin,2004; 62:324(刘韩星,孙晓琴,肖静,程志政,周建,欧阳世翕.化学学报,2004;62:324) |
| [14] | Kan Y M,Wang P L,Li Y X,Cheng Y B.JInorg Mater,2002;17:1063(阚艳梅,王佩玲,李永祥,程一兵.无机材料学报.2002;17:1063) |
| [15] | Aboujalil A,Deloume J P,Chassagneux F.J Mater Chem,1998; 8:1601 |
| [16] | Zhu L H,Huang Q W,Gu H.J Cryst Growth,2004; 267:199 |
| [17] | Song Y X,Li C N,Yan H X.J Inorg Mater,2002; 47:145(宋煜昕,李承恩,晏海学.无机材料学报,2002;47:145) |
| [18] | Kimura T,Takenaka A,Mifune T,Hayashi Y,Yamaguchi T.J Mater Sci,1992; 27:1479 |
| [19] | Ki H Y,Yong S C,Dong H K.J Mater Sci,1998; 33:2977 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%