采用熔体快淬方法制备4种厚度的Fee83Ga17合金薄带,研究了不同厚度薄带的组织结构和磁致伸缩性能.合金薄带的组织结构和磁致伸缩性能与快淬时的冷速密切相关,12 m/s制备的75 μm厚薄带的磁致伸缩系数λ值最高,达到了-2100×10-6;XRD和DSC分析确定了在厚度为45,55和75 μm薄带中出现了有序的D03结构相,75 μm厚薄带在669℃发生A2+D03→A2的相转变;对薄带组织形貌的观察发现,提高快淬的冷速有利于抑制富Ga相的析出.薄带样品大的磁致伸缩效应主要来源于析出的特殊D03结构相和薄带样品大的形状各向异性.
参考文献
| [1] | Guruswamy S,Srisukhumbowornchai N,Clark A E,Restorff J B,Wun-Fogle M.Scr Mater,2000; 43:239 |
| [2] | Han Z Y,Zhou S Z,Zhang M C,Gao X X.J Magn Mater Devices,2004; 35(1):15(韩智勇,周寿增,张茂才,高学绪.磁性材料及器件,2004;35(1):15) |
| [3] | Srisukhumbowornchai N,Guruswamya S.J Appl Phys,2002; 92:5371 |
| [4] | Kumagai A,Fujita A,Fukamichi K,Oikawa K,Kainuma R,Ishida K.J Magn Mater,2004; 272-276:2060 |
| [5] | Clark A E,Hathaway K B,Wun-Fogle M,Restorff J B,Lograsso T A,Keppens V M,Petculescu G,Taylor R A.J Appl Phys,2003; 93:8621 |
| [6] | Ikeda O,Kainuma R,Ohnuma I,Fukamichi K,Ishida K.J Alloy Compd,2002; 347:198 |
| [7] | Kellogg R A,Flatau A B,Clark A E,Wun-Fogle M,Lograsso T A.J Appl Phys,2002; 91:7821 |
| [8] | Cheng S F,Das B N,Wun-Fogle M,Lubitz P,Clark A E.IEEE Trans Magn,2002; 38:2838 |
| [9] | Liu G D,Li Y X,Hu H N,Qu J P,Liu Z H,Dai X F,Zhang M,Cui Y T,Chen J L,Wu G H.Acta Phys Sin,2004; 53:3191(刘国栋,李养贤,胡海宁,曲静萍,柳祝红,代学芳,张铭,崔玉亭,陈京兰,吴光恒.物理学报,2004;53:3191) |
| [10] | Lograsso T A,Ross A R,Schlagel D L,Clark A E,WunFogle M.J Alloy Compd,2003; 350:95 |
| [11] | Han Z Y,Zhang M C,Gao X X,Zhou S Z.Prog Nat Sci,2004; 14:593(韩智勇,张茂才,高学绪,周寿增.自然科学进展,2004;14:593) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%