采用激光熔化连续沉积工艺制备出了以Cr13Ni5Si2为初生相、以γ-Ni基固溶体为增韧相的金属硅化物耐磨合金,在室温干滑动磨损条件下测试了Cr13Ni5Si2/γ合金的耐磨性能并讨论了其磨损机理.结果表明,由于Cr13Ni5Si2/γ合金优良的强韧性配合以及在磨损过程中磨损表面上稳定氧化物转移覆盖层的快速形成,合金在室温干滑动磨损条件下具有优异的耐学性能和很低的载荷敏感系数.
参考文献
| [1] | Hawk J A,Alman D E.Mater Sci Eng,1997; A239-240:899 |
| [2] | Johnson B J,Kennedy F E,Baker I.Wear,1996; 192:241 |
| [3] | Hawk J A,Alman D E.Wear,1999; 225-229:544 |
| [4] | Alman D E,Hawk J A,Tylczak J H,Dogan C P,Wilson R D.Wear,2001; 251:875 |
| [5] | Yang J,La P Q,Liu W M,Xue Q J.Wear,2004; 257:104 |
| [6] | Jin J H,Stephenson D J.Wear,1998; 217:200 |
| [7] | Hawk J A,Alman D E.Scr Mater,1995; 5:725 |
| [8] | Alman D E,Hawk J A.Wear,2001; 251:890 |
| [9] | Kim J H,Tabaru T,Hirai H,Kitahara A,Hanada S.Scr Mater,2003; 48:1439 |
| [10] | Zhou J,Guo J T.Mater Sci Eng,2003; A339:166 |
| [11] | Misra A,Gibala R,Noebe R D.Intermetallics,2001; 9:971 |
| [12] | Xu H P,Ngan A H W,Duggan B J,Chen Q Z.Mater Lett,1997; 31:233 |
| [13] | Mishima Y,Kato M,Kimura Y,Hosoda H,Miura S.Intermetallics,1996; 4:171 |
| [14] | Villars P,Prince A,Okamoto H.Handbook of Ternary Alloys Phase Diagrams.New York:ASM International,1995:9143 |
| [15] | Tang H B,Fang Y L,Wang H M.Acta Mater,2004; 52:1773 |
| [16] | Wang H M,Zhang L Y.Chin Pat,No.02121496.4,2002(王华明,张凌云.中国发明专利,ZL 02121496.4,2002) |
| [17] | Zhang L Q,Wang H M.Mater Lett,2003; 57:2710. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%