对(Tb,Dy)Fe2超磁致伸缩合金,用微分相衬显微镜原位研究了应力和磁场引起的畴变、卸载压痕裂纹在湿空气中的滞后扩展以及在湿空气中恒磁场引起的滞后畴变及滞后开裂.结果表明,当磁场大于门槛值Hth后就能使压痕裂纹发生瞬时扩展;在湿空气中,残余应力能使(Tb,Dy)Fe2发生滞后扩展,当裂纹止裂后,恒磁场(H<Hth)能使磁畴发生滞后变化,并能使压痕裂纹进一步发生滞后扩展.
参考文献
[1] | Engdahl G.In:Mayergoyz I ed,Handbook of Giant Magnetostrictive Materials,New York:Academic Press,2000:1 |
[2] | Wang B W.Preparation and Devices Design of Giant Magnetostrictive Materials.Beijing:Metallurgical Industry Press,2003(王博文.超磁致伸缩材料制备与器件设计.北京:冶金工业出版社,2003) |
[3] | Wang B W,Yan R G.J Hebei Univ Technol,2004;33(2):16(王博文,闫荣格.河北工业大学学报,2004;33(2):16) |
[4] | Li K S,Li H W,Fang Y K.J Rare Earths,2004; 22:126 |
[5] | Wang Y,Chu W Y,Su Y J,Qiao L J.Mater Sci Eng,2002; B59:263 |
[6] | Wang Y,Chu W Y,Gao K W,Su Y J,Qiao L J.J Appl Phys,2003; 82:1583 |
[7] | Yang W.Mechatronic Reliability.Beijing:Tsinghua University Press,2001:14(杨卫.力电失效学.北京:清华大学出版社,2001:14) |
[8] | Wang R M,Chu W Y,Gao K W,Su Y J,Qiao L J.Mater Lett,2004; 58:1811 |
[9] | Wang R M,Chu W Y,Su Y J,Gao K W,Qiao L J.Acta Metall Sin,2005; 41:297(王瑞敏,褚武扬,宿彦京,高克玮,乔利杰.金属学报,2005;41:297) |
[10] | Chu W Y,Qiao L J,Chen Q Z,Gao K W.Fracture and Environment Fracture.Beijing:Science Press,2000:6(褚武扬,乔利杰,陈奇志,高克玮.断裂与环境断裂.北京:科学出版社,2000:6) |
[11] | Anstis G R,Chantikul P,Laun B R,Marshall D B.J Am Ceram Soc,1981; 64:533 |
[12] | Chantikul P,Anstis G R,Laun B R,Marshall D B.J Am Ceram Soc,1981; 64:539 |
[13] | Ma R Z,Jiang M H,Xu Z X.Functional Materials Generality.Beijing:Metallurgical Industry Press,1999:80(马如璋,蒋民华,徐祖雄.功能材料学概论.北京:冶金工业出版社,1999:80) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%