加入少量的Ce(0.2%-0.8%,质量分数)可明显细化α-Mg基体,随Ce量增加,合金中的β-Mg17Al12相数量减少,且由连续网状形态变为非连续分布.同时,Ce与合金中的Al结合形成针状或杆状的Al4Ce化合物.能谱分析和液淬显微组织观察表明,组织细化机制主要归结为Ce加入引起结晶界面前沿的成分过冷,增加均质形核的数量.显微组织的改善导致了合金的力学性能和腐蚀性能明显提高.
参考文献
| [1] | Polmear I J.Mater Sci Technol,1994; 1:1 |
| [2] | Mordike B L,Ebert T.Mater Sci Eng,2001; A302:37 |
| [3] | Edward J,Vinarci K.Light Met Age,2001; 4:74 |
| [4] | Dwain M.Magers.Light Met Age,1996; 5:60 |
| [5] | Bamberger M.Mater Sci Technol,2001; 1:15 |
| [6] | Tamura Y,Kono N,Motigi T,Sato E.Jpn Inst Light Met,1998; 48:395 |
| [7] | Tamura Y.Jpn Inst Light Met,1998; 48(8):185 |
| [8] | Nair K S,Mittal M C.Mater Sci Forum,1988; 30:89 |
| [9] | Wei L Y.Mater Sci Technol,1996; 12:741 |
| [10] | Pettersen G.Mater Sci Eng,1996; A207:115 |
| [11] | Wei L Y.J Alloys Compd,1996; 232:264 |
| [12] | Pettersen K,Lohne O,Ryum N.Metall Mater Trans,1999; 21A:221 |
| [13] | Song G,Atrens A,St John D,Wu X,Nairn J.Corros Sci,1997; 39:1981 |
| [14] | Ambat R,Aung N,Zhou W.Corros Sci,2000; 42:1433 |
| [15] | Song G,Atrens A,Wu X L,Zhang B.Corros Sci,1998;40:1769 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%