采用低温燃烧合成法,在柠檬酸-硝酸盐体系中合成了Ce1-xNdxO2-x/2(0≤x≤0.6)固溶体纳米粉体.X射线衍射(XRD)结果表明,Nd3+取代Ce4+形成具有单相立方萤石结构的固溶体,其晶格常数随Nd3+掺杂浓度的增大而线性增加,晶粒尺寸在15-24 nm之间.透射电镜(TEM)结果表明,粉体颗粒尺寸在20-40 nm之间,分散性较好,具有较高的烧结活性.Raman光谱结果表明,F2g宽化峰的出现与掺杂后固溶体中产生的氧空位有关,并且随着掺杂浓度的增加,氧空位数量也随之增加.X射线荧光光谱(XRF)的分析表明,实际掺杂浓度非常接近原始化学计量比.
参考文献
| [1] | Inaba H,Tagawa H.Solid State Ionics,1996; 83:1 |
| [2] | Van herle J,Horita T,Kawada T,Sakai N,Yokokawa H,Dokiya M.Solid State Ionic,1996; 86:1255 |
| [3] | Lin X M,Li L P,Li G S,Su W H.Mater Chem Phys,2001,69:236 |
| [4] | Shuk P,Greenblatt M.Solid State Ionics,1999; 116:217 |
| [5] | Chavan S V,Tyagi A K.J Mater Res,2004; 19(2):474 |
| [6] | Tao Y,Zhao G W,Zhang W P.Mater Res Bull,1997; 32:501 |
| [7] | Lamas D G.J Mater Sci Lett,2001; 20:1447 |
| [8] | Bianchetti M F,Juárez R E,Lamas D G,de Reca N E W Perez L,Cabanillas E.J Mater Res,2002; 17:2185 |
| [9] | Purohit R D,Sharma B P,Pillai K T.Mater Res Bull,2001; 36:2711 |
| [10] | Fu Y P,Lin C H.J Alloy Compd,2003; 354:232 |
| [11] | Rocha R A,Muccillo E N S.Br Ceram Trans,2003;102(5):216 |
| [12] | Trovarelli A,Zamar F,Llorca J.J Catal,1997; 169:490 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%