通过充氢和未充氢缺口拉伸试样和三点弯曲试样在SEM下的原位加载,研究了氢对Zr65Al7.5Ni10Cu17.5块体非晶合金形变和开裂过程的影响.结果表明,无论是否有氢,块体非晶的剪切带发展到临界尺寸,剪切裂纹就沿剪切带形核、扩展,它一旦张开就导致快速的断裂.断口边缘观察到的无特征区是剪切带,而不是剪切裂纹断口;剪切断口形貌和拉伸断口形貌没有本质区别.只有当长时间充氢才能形成氢鼓泡,如鼓泡很小或尚未形成,则氢对剪切带以及裂纹的形核、扩展没有明显影响;如存在较大的氢鼓泡,则当剪切带尚未充分发展时微裂纹就形核,导致低应力脆断.
参考文献
| [1] | Vaidyanathan R,Dao M,Ravichandran G,Suresh S.Acta Mater,2001; 49:3781 |
| [2] | Flores K M,Dauskardt R H.Scr Mater,1999,41:937 |
| [3] | Spaepen F.Acta Metall,1977; 25:407 |
| [4] | Inoue A,Zhang W,Zhang T,Kurosaka K.Acta Mater,2001; 49:2645 |
| [5] | Xing L Q,Li Y,Ramesh K T,Li J,Hufnagel T L.Phys Rev,2001; 64B:180201 |
| [6] | Wright W J,Schwarz R B,Nix W D.Mater Sci Eng,2001;A319-321:229 |
| [7] | Flores K M,Dauskardt R H.Acta Mater,2001; 49:2527 |
| [8] | Li J X,Chu W Y,Gao K W,Qiao L J.Acta Metall Sin,2003; 39:359(李金许,褚武扬,高克玮,乔利杰,金属学报,2003;39:359) |
| [9] | Li J X,Shan G B,Gao KW,Qiao L J,Chu W Y.Mater Sci En9,2003; A354:337 |
| [10] | Namboodhiri T K,Ramesh T A,Singh G,Seghal S.Mater Sci Eng,1983; 61:23 |
| [11] | Lin J J,Perng T P.Metall Mater Trans,1995; 26A:197 |
| [12] | Suh D,Danskardt R H.Scr Mater,2000; 42:233 |
| [13] | Guo J X,Li J X,Qiao L J,Gao K W,Chu W Y.Corros Sci,2003; 45:735 |
| [14] | Eliaz N,Banks-Sills L,Ashkenazi D,Eliasi R.Acta Mater,2004; 52:93 |
| [15] | Shan G.B,Wang Y W,Chu W Y,Li J X,Hui X D.Corros Sci,2005; 47:2731 |
| [16] | Peng X,Su Y J,Gao K W,Qiao L J,Chu W Y.Mater Lett,2004; 58:2073 |
| [17] | Creager M,Paris P C.Int J Fract Mech,1967; 4:247 |
| [18] | Wang Y W,Chu W Y,Li J X,Su Y J,Gao K W,Qiao L J.Mater Lett,2004; 58:2393 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%