通过拉伸实验研究了电场退火(850 ℃,25 min)对IF深冲钢板塑性应变比(r值)的影响.结果表明,电场退火提高了IF深冲钢板的平均塑性应变比((-r)值).这主要是由于电场退火显著增强了有利于IF深冲钢板塑性应变比的再结晶γ纤维织构{111}
参考文献
| [1] | Hutchinson W B.Int Met Rev,1982; 27:307 |
| [2] | Urabe T,Jonas J J.ISIJ Int,1994; 34:435 |
| [3] | Ray R K,Jonas J J,Hook R E.Int Met Rev,1994; 39:129 |
| [4] | Conrad H,Karam N,Mannan S.Scr Metall,1983; 17:411 |
| [5] | Lu H A,Conrad H.Appl Phys Lett,1991; 59:47 |
| [6] | Conrad H,Guo Z,Sprecher A F.Scr Metall,1989; 23:821 |
| [7] | Li M Q,Wu S.Scr Metall Mater,1994; 31:75 |
| [8] | Liu W,Liang K M,Zheng Y K,Cui J Z.Scr Mater,1996;15:1327 |
| [9] | He C S,Zhang Y D,Wang Y N,Zhao X,Zuo L,Esling C.Scr Mater,2003; 48:737 |
| [10] | Whiteley R L.Trans ASM,1960; 52:154 |
| [11] | Schulz L G.J Appl Phys,1949; 20:1030 |
| [12] | Liang Z D,Xu J Z,Wang F.Three Dimensional Orientation Distribution Analysis of Textured Materials-ODF Analysis.Shenyang:Northeast University of Technology Press,1986:108 (梁志德,徐家祯,王福.织构材料的三维取向分析术-ODF分析.沈阳:东北工学院出版社,1986:108) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%