利用电解沉积技术制备出系列亚微米晶纯铜样品,并在样品中引入不同密度的纳米孪晶.室温轧制具有不同孪晶密度的纯铜样品,使样品中储存大量位错.结果表明,具有高密度纳米孪晶结构的纯铜样品,40%轧制变形可使其屈服强度从690MPa增加到850 MPa;而无孪晶的亚微米铜样品的屈服强度在同样轧制变形条件下只从230 MPa增加到330 MPa.这表明具有高密度纳米孪晶结构的纯铜样品具有很高的位错储存能力.
参考文献
[1] | Mayers M A,Chawla K K.Mechanical Behavior of Materials.Upper Saddle River,NJ:Prentice Hall,Inc.,1999:291 |
[2] | Sanders P G,Eastman J A,Weertman J R.Acta Mater,1997; 45:4019 |
[3] | Legros M,Elliott B R,Rittner M N,Weertman J R,Hemker K J.Philos Mag,2000; 80A:1017 |
[4] | Kumar K S,Suresh S,Chisholm M F,Horton J A,Wang P.Acta Mater,2003; 51:387 |
[5] | van Swygenhoven H,Derlet P M,Hasnaoui A.Acta Mater,2004; 52:2251 |
[6] | Yamakov V,Wolf D,Phillpot S E,Mukherjee A K,Gleiter H.Nature Mater,2002; 1:1 |
[7] | Budrovic Z,van Swygenhoven H,Derlet P M,van Petegem S,Schmitt B.Science,2004; 304:273 |
[8] | Wang Y M,Ma E,Chen M W.Appl Phys Lett,2002; 80:2395 |
[9] | Jia D,Wang Y M,Ramesh K T,Ma E,Zhu Y T,Valiev R.Appl Phys Lett,2001; 79:611 |
[10] | Valiev R Z,Islamgaliev R K,Alexandrov I V.Prog Mater Sci,2000; 45:103 |
[11] | Lu L,Shen Y F,Chen X H,Qian L H,Lu K.Science,2004; 304:422 |
[12] | Shen Y F,Lu L,Lu Q H,Jin Z H,Lu K.Scr Mater,2005;52:989 |
[13] | Lu L,Schwaiger R,Shan Z W,Dao M,Lu K,Suresh S.Acta Mater,2005; 52:2169 |
[14] | Ananthan V S,Leffers T,Hansen N.Mater Sci Technol,1991; 7:1069 |
[15] | Babyak W J,Rhines F N.TMS AIME,1960; 218:21 |
[16] | Zhang X,Misra A,Wang H,Lima A L,Hundley M F,Hoagland R G.Appl Phys Lett,2004; 84:1096 |
[17] | Ma E,Wang Y M,Lu Q H,Sui M L,Lu L,Lu K.Appl Phys Lett,2004; 85:4932 |
[18] | Christian J W,Mahajan S.Prog Mater Sci,1995; 39:1 |
[19] | Park K T,Park J H,Lee Y S,Nam W J.Mater Sci Eng,2005; A408:102 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%