为改善铸态AZ91镁合金的力学性能和成形加工性能,对铁模铸造试样进行了均匀化退火处理,退火温度范围为350-450℃,退火时间范围为5-24 h.均匀化退火后Mg17Al12相呈细小的颗粒状分布在α-Mg基体上,枝晶偏析大部分得到消除.力学性能实验结果表明,铸态AZ91镁合金的抗拉强度约为163 MPa,延伸率为3.2%;经过380℃,15 h均匀化退火,可获得最高延伸率达11.2%,抗拉强度243 MPa;经过420℃,5 h均匀化退火,可获得最高强度达246 MPa,延伸率达10%.
参考文献
| [1] | Agfion E,Bronfin B.Mater Sci Forum,2000; 350-351:19 |
| [2] | Cahn R W,Haasen P,Kramer E J.Materials Science and Technology.New York:VCH Publishers Inc,1996 |
| [3] | Mordike B L,Ebert T.Mater Sci Eng,2001; A302:37 |
| [4] | Dahle A K,Lee Y C,Nave M D,Schaffer P L,St John D H.J Light Met,2001; (1):61 |
| [5] | Yan Y Q,Zhang T J,Zhou L,Deng J.Rare Met,2004;23:220 |
| [6] | Lü Y Z,Wang Q D,Ding W J.Mater Lett,2000; 44:265 |
| [7] | Zhang Y Z,Zhang K,Cui D J,Wu X P,Fan J Z,Cui B,Zheng Y X,Lei J.Foundry,2000; 49(12):74(张永忠,张奎,崔代金,吴绪平,樊建中,崔波,郑宇新,雷健.铸造,2000;49(12):74) |
| [8] | Huang G S,Wang L Y,Huang G J,Pan F S.J Chongqing Univ (Nat Sci),2004; 27(11):18(黄光胜,汪凌云,黄光杰,潘复生.重庆大学学报(自然科学版),2004;27(11):18) |
| [9] | Peng J,Zhang D F,Yang C M,Ding P D.J Mater Eng,2004; (8):32(彭建,张丁非,杨椿楣,丁培道.材料工程,2004;(8):32) |
| [10] | Xie J X,Liu X F,Wang Z X,Jin J B.China Pat,CN200510126459.7,2005-12-12(谢建新,刘雪峰,王智祥,金军兵.中国发明专利,CN200510126459.7,2005-12-12) |
| [11] | Liu Z,Zhang K,Zeng X Q.Theoretical Basis and Applications of Magnesium-Base Alloys.Beijing:China Machine Press,2002(刘正,张奎,曾小勤.镁基轻质合金理论基础及其应用.北京:机械工业出版社,2002) |
| [12] | Cho S S,Chun B S,Won C W.J Mater Sci,1999; 34:4311 |
| [13] | Duly D,Brechet Y.Acta Metall Mater,1994; 42:3035 |
| [14] | Duly D,Simon J P,Brechet Y.Acta Metall Mater,1995;43:101 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%