采用外加恒电位下腐蚀电流-温度扫描方法研究了在0.5%Cl-溶液中,SO2-4浓度对316不锈钢点腐蚀行为的影响结果表明,随着SO2-4浓度的增加,钝化电流增加,开路电位降低.当SO2-4浓度低于0.42%时,316不锈钢的临界点蚀温度比不存在SO2-4时的临界点蚀温度低;当SO2-4浓度大于0.42%时,临界点蚀温度比不存在SO2-4时的临界点蚀温度高.从离子竞争吸附的角度进行分析,对SO2-4加速与抑制点蚀两种作用规律的形成原因进行了解释.
参考文献
| [1] | Garfias-Mesias L F,Sykes J M.Corros Sci,1999; 41:959 |
| [2] | Burstein G T,Pistorius P C,Mattin S P.Corros Sci,1993;35:57 |
| [3] | Abd E I,Meguid E A,Mahmoud N A,Gouda V K.Br Corros J,1998; 33:42 |
| [4] | Li M C,Zeng C L,Lin H C,Cao C N.Acta Metall Sin,2002:36:1287(李谋成,曾潮流,林海潮,曹楚南.金属学报,2002;36:1287) |
| [5] | Liu G Q,Zhu Z Y,Ke W.Acta Metall Sin,2001; 37:272(刘国强,朱自勇,柯伟金属学报,2001;37:272) |
| [6] | Sherbini E E,Rehim S S.Corros Sci,2000; 42:785 |
| [7] | Lee W J,Pyun S I.Electrochim Acta,2000; 45:1901 |
| [8] | Pyun S-I,Park J-J.J Solid State Eletrochem,2004; 8:296 |
| [9] | Ernst P,Newman R C.Corros Sci,2002; 44:943 |
| [10] | Anderko A,Sridhar N,Dunn D S.Corros Sci,2004; 46:1583 |
| [11] | Burstein G T,Moloney J J.Electrochem Commun,2004;6:1037 |
| [12] | Wu J W,Li X G,Du C W,WangS,Song Y Q.J Mater Sci Technol,2005; 21:28 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%